Coated steel member, coated steel sheet, and methods for manufacturing same

ABSTRACT

The present invention has as its object the provision of a coated steel member and coated steel sheet excellent in hydrogen embrittlement resistance in a corrosive environment and methods for manufacturing the same. The coated steel member of the present invention is provided on its surface with an Al—Fe-based coating containing Cu and one or more of Mo, Ni, Mn, and Cr in a total by mass % of 0.12% or more by heating, cooling, and manufacturing a coated steel sheet having a layer containing Cu on its surface under predetermined conditions.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a Divisional of copending application Ser. No. 17/291,507, filed on May 5, 2021, which is the National Phase under 35 U.S.C. § 371 of International Application No. PCT/JP2020/004427, filed on Feb. 5, 2020, which claims the benefit under 35 U.S.C. § 119(a) to Patent Application No. 2019-018995, filed in Japan on Feb. 5, 2019, all of which are hereby expressly incorporated by reference into the present application.

FIELD

The present invention relates to a coated steel member, coated steel sheet, and methods for manufacturing the same.

BACKGROUND

In the field of steel sheets for automobile use, due to the recent increasing severity of environmental regulations and collision safety standards, applications of steel sheet having high tensile strength are increasing so as to achieve both fuel efficiency and collision safety. However, along with the higher strength, the press formability of steel sheet falls, so it has become difficult to manufacture products with complicated shapes.

Specifically, due to the drop in ductility of steel sheet accompanying higher strength, the problem arises of fracture of the highly worked portions. Further, due to the residual stress after working, the problems arise that springback and wall camber occur and the dimensional precision deteriorates. Therefore, it is not easy to press form steel sheet having a high strength, in particular a tensile strength of 780 MPa or more, into a product having a complicated shape. Note that, if using not press forming, but roll forming, high strength steel sheet is easily worked, but applications have been limited to parts having uniform cross-sections in the longitudinal direction.

Therefore, in recent years, for example, as disclosed in PTLs 1 to 3, hot stamping has been employed as art for press-forming materials which are difficult to shape such as high strength steel sheet. Hot stamping is a hot shaping technology for heating a material before shaping, then shaping the material.

In this art, the material is heated, then shaped, so at the time of shaping, the steel material is soft and has good shapeability. Due to this, even if a high strength steel material, it is possible to precisely form it into a complicated shape. Further, in hot stamping, a press die is used for hardening during shaping, so after the shaping, the steel material has sufficient strength.

For example, according to PTL 1, hot stamping can be used to impart a tensile strength of 1400 MPa or more to a steel material after shaping.

CITATIONS LIST Patent Literature

-   [PTL 1] Japanese Unexamined Patent Publication No. 2002-102980 -   [PTL 2] Japanese Unexamined Patent Publication No. 2012-180594 -   [PTL 3] Japanese Unexamined Patent Publication No. 2012-1802 -   [PTL 4] Japanese Unexamined Patent Publication No. 2003-183802 -   [PTL 5] Japanese Unexamined Patent Publication No. 2004-124208 -   [PTL 6] Japanese Unexamined Patent Publication No. 2012-62500 -   [PTL 7] Japanese Unexamined Patent Publication No. 2003-268489 -   [PTL 8] Japanese Unexamined Patent Publication No. 2017-179589 -   [PTL 9] Japanese Unexamined Patent Publication No. 2015-113500 -   [PTL 10] Japanese Unexamined Patent Publication No. 2017-525849 -   [PTL 11] Japanese Unexamined Patent Publication No. 2011-122207 -   [PTL 12] Japanese Unexamined Patent Publication No. 2011-246801 -   [PTL 13] Japanese Unexamined Patent Publication No. 2012-1816

SUMMARY Technical Problem

At the present time, along with the establishment of challenging fuel efficiency targets in various countries, further higher strength steel materials are being demanded for lightening the weight of car bodies. Specifically, high strength steel materials of over the general strength of 1.5 GPa in hot stamping are considered necessary.

In this regard, if applying high strength steel materials of over a strength of 1 GPa to automobiles, not only the above-mentioned shapeability and toughness after shaping, but also hydrogen embrittlement resistance is demanded. If the hydrogen embrittlement resistance of high strength steel sheet is not sufficient, after an automobile is shipped to the market, the steel will corrode during use by the general user and the hydrogen generated along with the corrosion reaction may cause embrittlement cracking.

In a region over a strength of 1.5 GPa, the sensitivity of a steel material to hydrogen embrittlement rapidly increases, so hydrogen embrittlement cracking is a concern even at a surface coated steel sheet having corrosion resistance. Therefore, to commercially apply high strength steel materials of over 1.5 GPa to car bodies, art is necessary for providing a coated steel member provided with the conventional or better corrosion resistance and excellent in hydrogen embrittlement resistance in a corrosive environment.

Regarding high strength steel materials of over 1.5 GPa, for example, in PTL 2, a press formed article excellent in toughness and having a tensile strength of 1.8 GPa or more which is formed by hot pressing is disclosed. However, the measures against hydrogen embrittlement in a corrosive environment are not sufficient. In use as an automobile member, sometimes greater safety demands are not answered.

Further, in PTL 3, a steel material having an extremely high tensile strength of 2.0 GPa or more and further having excellent toughness and ductility is disclosed. However, the measures against hydrogen embrittlement in a corrosive environment are not sufficient. In use as an automobile member, sometimes greater safety demands are not answered.

Regarding corrosion resistance, for example in PTL 4, high strength Al-plated steel sheet excellent in corrosion resistance after coating is disclosed. However, there is no description regarding hydrogen embrittlement resistance. This is unsuitable for actual use of a high strength material of over 1.5 GPa.

Further, in PTL 5, high strength surface treated steel sheets having Ni, Cu, Cr, and Sn layers excellent in corrosion resistance after coating are disclosed and in PTL 6, Ni, Cr, Cu, and Co plated coated steel materials are disclosed. However, there are no descriptions regarding hydrogen embrittlement resistance. These are unsuitable for actual use of a high strength material of over 1.5 GPa.

Regarding hydrogen embrittlement resistance, for example, in PTLs 7, 8, and 9, hot stamped materials excellent in hydrogen embrittlement resistance in a hydrochloric acid immersion environment are disclosed. However, the hydrogen embrittlement resistance in an air corrosive environment and the hydrogen embrittlement resistance in a solution immersion environment of hydrochloric acid etc. often do not match. These materials are unsuitable for practical use of high strength materials of over 1.5 GPa.

Further, in PTL 10, a hot stamping material with the Ni in the steel concentrated at the surface layer is disclosed and it is described that this has the effect of suppressing hydrogen penetration at the time of heating in the hot stamping process. However, there is no description relating to the hydrogen embrittlement resistance in a corrosive environment at the time of actual use. This is unsuitable for actual use of a high strength material of over 1.5 GPa.

Further, in PTLs 11, 12, and 13, hot stamping materials in which Ni diffuses from an Ni-based plating layer to the surface layer of the steel sheet is disclosed and it is described that this has the effect of suppressing hydrogen penetration in a corrosive environment. However, the hydrogen embrittlement resistance of the steel material is not sufficient, so this is unsuitable for actual use of a high strength steel material of over 1.5 GPa.

The present invention was made so as to solve the above problem and has as its object the provision of a coated steel member and coated steel sheet having high tensile strength and excellent in hydrogen embrittlement resistance in a corrosive environment and methods for manufacturing the same.

Solution to Problem

The present invention has as its gist the following coated steel member, coated steel sheet, and methods for manufacturing the same. Below, steel sheet which is not coated and is used as a material of coated steel sheet will be simply referred to as “steel sheet”.

(1) A coated steel member comprising an Al—Fe-based coating on its surface, the Al—Fe-based coating containing Cu and one or more of Mo, Ni, Mn, and Cr in a total by mass % of 0.12% or more, the contents of Cu, Mo, Ni, Mn, and Cr satisfying, by mass %, Cu+0.01×63.5(Mo/95.9+Ni/58.7+Mn/54.9+Cr/52.0)≥0.12%.

(2) The coated steel member of (1) wherein a thickness of the Al—Fe-based coating is 10 to 100 μm and the chemical composition of the Al—Fe-based coating satisfies, by mass %, an average value of Al content in a thickness direction: 20.0% or more, an average value of Fe content in the thickness direction: 50.0% or more, a minimum value of Cu content in the thickness direction: 0.06% or more, and a ratio of a maximum value and minimum value of Cu content in the thickness direction: 1.4 or more.

(3) The coated steel member of (1) or (2) wherein a chemical composition of the part of the coated steel member other than the Al—Fe-based coating comprises, by mass %, C: 0.25 to 0.60%, Si: 0.25 to 2.00%, Mn: 0.30 to 3.00%, P: 0.050% or less, S: 0.0100% or less, N: 0.010% or less, Ti: 0.010 to 0.100%, B: 0.0005 to 0.0100%, Mo: 0.10 to 1.00%, Cu: 0.01 to 1.00%, Cr: 0 to 1.00%, Ni: 0 to 1.00%, V: 0 to 1.00%, Ca: 0 to 0.010%, Al: 0 to 1.00%, Nb: 0 to 0.10%, Sn: 0 to 1.00%, W: 0 to 1.00%, Sb: 0 to 1.00%, REMs: 0 to 0.30%, and balance: Fe and impurities.

(4) The coated steel member of any of (1) to (3) wherein the Al—Fe-based coating contains, by mass %, Si in 1 to 20%.

(5) A coated steel sheet having a layer where Cu is concentrated at a surface of a steel sheet, having a degree of Cu surface concentration at the layer where Cu is concentrated of 1.2 or more, further having an Al-based coating on the layer where Cu is concentrated, and having an average crystal grain size of the steel sheet of 30 μm or less. Here, the “degree of Cu surface concentration” shows the ratio of (maximum content of Cu in range from surface of steel sheet to depth of 0 to 30 μm)/(average content of Cu from surface of steel sheet to depth of 200 μm), while the “surface of steel sheet” means the position of a depth where the Fe content becomes 90% when performing GDS from the surface of the coated steel sheet in the thickness direction.

(6) A coated steel sheet comprised of a steel sheet, an intermediate layer positioned on a surface of the steel sheet, and an Al-based coating positioned on a surface of the intermediate layer, the intermediate layer containing Cu, the intermediate layer containing Cu and one or more of Mo, Ni, Mn, and Cr in a total by mass % of 30% or more.

(7) A coated steel sheet comprised of a steel sheet and an Al-based coating positioned on a surface of the steel sheet, the Al-based coating containing Cu, the Al-based coating containing Cu and one or more of Mo, Ni, Mn, and Cr in a total by mass % of 1.0% or more.

(8) The coated steel sheet of any of (5) to (7) wherein a chemical composition of the steel sheet comprises, by mass %, C: 0.25 to 0.60%, Si: 0.25 to 2.00%, Mn: 0.30 to 3.00%, P: 0.050% or less, S: 0.0100% or less, N: 0.010% or less, Ti: 0.010 to 0.100%, B: 0.0005 to 0.0100%, Mo: 0.10 to 1.00%, Cu: 0.01 to 1.00%, Cr: 0 to 1.00%, Ni: 0 to 1.00%, V: 0 to 1.00%, Ca: 0 to 0.010%, Al: 0 to 1.00%, Nb: 0 to 0.10%, Sn: 0 to 1.00%, W: 0 to 1.00%, Sb: 0 to 1.00%, REMs: 0 to 0.30%, and balance: Fe and impurities.

(9) A method for manufacturing the coated steel sheet of (5), the method comprising the steps of: heating a slab at 1100 to 1350° C., hot rolling the heated slab to obtain hot rolled steel sheet under conditions where, when defining a time t₁ (hr) from an end of rough rolling to a start of finish rolling and an average temperature T₁ (° C.) of a rough bar from the end of rough rolling to the start of finish rolling, (T₁+273)×(log t₁+20)≥20000 and a finish rolling end temperature becomes an Ar₃ point to 1000° C., cooling the above hot rolled steel sheet by an average cooling rate of 10° C./s, coiling the steel sheet after cooling at 700° C. or less, and pickling the steel sheet after coiling.

(10) The method of (3) wherein in the step of pickling hydrochloric acid or sulfuric acid is used, a pickling temperature is 80 to 90° C., and an acid concentration α (%) and pickling time “t” (s) satisfy 6≤α<14, 0<t≤20-30×α.

(11) A method for manufacturing the coated steel member of any of (1) to (4), the method comprising the steps of: heating the coated steel sheet of any of (5) to (8) under conditions where, when defining a peak temperature as T₂ (° C.) and a time from when a temperature of the coated steel sheet reaches a temperature lower by 10° C. from T₂ (° C.) as t₂ (hr), (T₂+273−10)×(log t₂+20)≥19000, an Ac₃ point≤T₂≤(Ac₃ point+300°) C., and an average rate of temperature rise 5 to 1000° C./s, and cooling the heated coated steel sheet down to an Ms point by an average cooling rate made an upper critical cooling rate or more, then cooling from the Ms point down to 100° C. or less by an average cooling rate of 5° C./s or more.

(12) The method of (11), wherein the coated steel sheet is hot shaped during cooling down to the Ms point.

Advantageous Effects of Invention

According to the present invention, it is possible to provide a coated steel member and coated steel sheet having high tensile strength and excellent in hydrogen embrittlement resistance in a corrosive environment and methods for manufacturing the same.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is a view showing the relationship between acid concentration and time in pickling in the present invention.

DESCRIPTION OF EMBODIMENTS

First, details of studies by the inventors in investigating the effects of chemical constituents and structure on properties so as to obtain a coated steel member having a high tensile strength and excellent in hydrogen embrittlement resistance in a corrosive environment will be explained.

Most of the steel sheet for hot stamping produced in Japan and overseas aiming at corrosion resistance are surface coated steel sheet obtained by aluminum coating or galvanization. If these coated steel sheet are hot stamped, alloying reactions proceed at the surface and a coated steel member having an Al—Fe-based coating or Zn—Fe-based plating is obtained. Note that most steel sheet are similar in chemical composition and exhibit strengths of the 1.5 GPa class after hot stamping due to C, which is included in 0.20 mass % or so.

(a) The inventors engaged in detailed studies for further lightening the weight of car bodies by increasing C to 0.25 mass % or more and applying over 1.5 GPa high strength steel materials to the bodies of automobiles. As a result, it was learned that even when applying an Al-based or Zn-based coating such as explained above, there is a high risk of hydrogen embrittlement cracking.

In the strength region over a strength of 1.5 GPa, the susceptibility of a steel material to hydrogen embrittlement rapidly increases. Embrittlement cracking occurs even with a trace amount of hydrogen produced, so it was guessed that even when applying an Al-based or Zn-based coating such as explained above, the corrosion resistance is not sufficient and hydrogen embrittlement cracking occurs due to a trace amount of hydrogen at a portion where moderate corrosion has progressed.

(b) The inventors tackled the improvement of corrosion resistance based on the mechanism of hydrogen embrittlement in a corrosive environment of a high strength steel material of over 1.5 GPa described above. As a result, they discovered that by including Cu in the surface Al—Fe-based coating of a coated steel member, the corrosion resistance is greatly improved and the hydrogen embrittlement resistance in a corrosive environment can be dramatically raised.

(c) Furthermore, the inventors discovered that if including the corrosion resistance elements of Mo, Ni, Mn, and Cr in the above Al—Fe-based coating in addition to Cu, the corrosion resistance is further improved. Further, in addition to the corrosion resistance, they optimized the chemical composition and structure of steel materials with a strength over 1.5 GPa to reduce the susceptibility to hydrogen embrittlement. That is, they improved the corrosion resistance over a conventional Al—Fe-based coating to prevent production of hydrogen accompanying a corrosion reaction and improved the hydrogen embrittlement resistance of steel materials even if hydrogen is generated and thereby developed technology for withstanding actual use of automobiles etc. even in a corrosive environment.

The present invention was made based on the above findings. Below, the requirements of the coated steel member, coated steel sheet, and methods for manufacturing the same according to one embodiment of the present invention will be explained in detail.

(A) Coated Steel Member

(A1) Coating of Coated Steel Member

The coated steel member according to the present embodiment has on its surface an Al—Fe-based coating containing Cu and one or more of Mo, Ni, Mn, and Cr in a total by mass % of 0.12% or more so as to satisfy the following formula (1). Note that, in the following explanation, the “%” regarding content will mean “mass %”. Further, an “Al—Fe-based coating” is a coating mainly comprised of Al and Fe. The Al and Fe are preferably included in a total of 70% or more. Further, an “Al—Fe-based coating” also means a film, alloyed plated layer, or intermetallic compound layer.

Cu+0.01×63.5(Mo/95.9+Ni/58.7+Mn/54.9+Cr/52.0)≥0.12%  formula (1)

The element symbols in the formula (1) show the contents of the elements of the Al—Fe-based coating (mass %). Further, below, the left side of formula (1) will be called the “concentration of corrosion resistance elements”.

An Al—Fe-based coating provided on the surface of a coated steel member and containing the corrosion resistance elements Cu and Mo, Ni, Mn, and Cr exhibits excellent corrosion resistance at the time of use of the member and has the effect of improving the hydrogen embrittlement resistance in a corrosive environment. If the concentration of corrosion resistance elements in the Al—Fe-based coating is less than 0.12%, the corrosion resistance at the time of use of the member will not be sufficient and the risk of hydrogen embrittlement accompanying corrosion will rise. Therefore, the concentration of corrosion resistance elements in the Al—Fe-based coating is made 0.12% or more. Preferably, it is 0.14% or more. The upper limit of the concentration of corrosion resistance elements is not particularly prescribed, but if over 1%, sometimes the above effect becomes saturated and the economicalness falls.

The Al—Fe-based coating may further contain Si in 1.0 to 20.0%. As explained later, the Al-based coating of coated steel sheet often has Si added to it. In that case, the Al—Fe-based coating of the coated steel member also contains Si. In an Al—Fe-based coating containing Si, the crystal structures of the intermetallic compounds become dense and there is the effect that the corrosion resistance is improved. Note that, even if Si is contained in 1 to 20%, if the above-mentioned concentration of corrosion resistance elements is 0.12% or more, the hydrogen embrittlement resistance in a corrosive environment becomes excellent. Note that, chemical composition of the Al—Fe-based coating is, by average value in the thickness direction, by mass %, Si: 0 to 20.0%, Cu: 0.06 to 3.0%, Mo: 0 to 5.0%, Ni: 0 to 5.0%, Mn: 0 to 8.0, Cr: 0 to 8.0%, Al: 5.0 to 60.0%, Fe: 30.0 to 90.0%, and a balance of impurities where Al+Fe: 70.0% or more. Al+Fe, that is, the total of the content of Al and the content of Fe, may be made 75.0% or more, 80.0% or more, or 85.0% or more.

The concentration of corrosion resistance elements in the Al—Fe-based coatings and the content of Si can be found in the following way.

GDS (glow discharge optical emission spectrometry) is performed in the thickness direction from the surface of the coated steel member to find the maximum contents of Cu, Mo, Ni, Mn, Cr, and Si in the Al—Fe-based coating. The measurement by GDS is performed at five random points at a position of ¼ of the sheet width (short side) from an end of the coated steel member in the width direction, the maximum amounts of Cu, Mo, Ni, Mn, and Cr in the Al—Fe-based coating at the different points were found, and the average values of the different elements at the five points were used by the formula (1) to find the concentration of corrosion resistance elements in the Al—Fe-based coating. Note that, “Al—Fe-based coating” shall mean the region where the content of Fe becomes less than 90% when performing GDS from the surface of the coated steel member. Note that, at the surface most layer, sometimes oxide scale and impurities are present, so the content of O is also measured and measurement values of the concentration of corrosion resistance elements in the range of thickness where the content of 0 is 1.0% or more are excluded.

The thickness of the Al—Fe-based coating is preferably 10 μm or more or 30 μm or more and preferably 100 μm or less or 80 μm. The content of Al in the Al—Fe-based coating is, by average value in the thickness direction, preferably 20.0% or more, 30.0% or more, or 40.0% or more while the content of Fe in the Al—Fe-based coating is preferably 50% or more or 60.0% or more.

The Al—Fe-based coating of the coated steel member of the present invention, as explained above, contains Cu. Due to this, it is possible to raise the hydrogen embrittlement resistance in a corrosive environment. By making the content of Cu near the boundary of the Al—Fe-based coating and steel sheet higher, it is possible to further lower the risk of hydrogen embrittlement. Specifically, in the Al—Fe-based coating, the minimum value of the content of Cu in the thickness direction is preferably made 0.06% or more and the ratio of the maximum value and minimum value of the content of Cu in the thickness direction is preferably made 1.4 or more.

(A2) Chemical Composition of Coated Steel Member

The reasons for limitation of the elements of the coated steel member according to the present embodiment are as follows. Here, the “chemical composition of the coated steel member” shall mean the average chemical composition of the part of the coated steel member other than the Al—Fe-based coating at the surface.

C: 0.25 to 0.60%

C is an element which raises the hardenability of steel and improves the strength of the coated steel member after hardening. However, with a content of C of less than 0.25%, it becomes difficult to secure sufficient strength in the coated steel member after hardening. Therefore, the content of C is made 0.25% or more. On the other hand, if the content of C is over 0.60%, the strength of the coated steel member after hardening becomes too high and the toughness and hydrogen embrittlement resistance remarkably deteriorate. Therefore, the content of C is made 0.60% or less. The content of C is preferably 0.29% or more or 0.31% or more and is preferably 0.55% or less, 0.50% or less, 0.48% or less, or 0.44% or less.

Si: 0.25 to 2.00%

Si is an element which is effective for raising the hardenability of steel and stably securing the strength after hardening. To obtain this effect, Si must be included in 0.25% or more. However, if the content of Si in the steel is over 2.00%, at the time of heat treatment, the heating temperature required for austenite transformation becomes remarkably high. Due to this, sometimes a rise in costs required for heat treatment is invited. Furthermore, a deterioration of toughness of the hardened part is invited. Therefore, the content of Si is made 2.00% or less. The content of Si is preferably 0.30% or more or 0.35% or more and is preferably 1.60% or less, 1.00% or less, 0.80% or less, or 0.60% or less.

Mn: 0.30 to 3.00%

Mn is an element which is extremely effective for raising the hardenability of steel sheet and stably securing the strength after hardening. Furthermore, it is an element lowering the Ac₃ point and promoting lowering of the hardening treatment temperature. Further, it has the effect of diffusing in an Al—Fe-based coating to improve the corrosion resistance. However, if the content of Mn is less than 0.30%, this effect is not sufficiently obtained. On the other hand, if the content of Mn is over 3.00%, the above effect becomes saturated and a deterioration of toughness or hydrogen embrittlement resistance of the hardened part is invited. Therefore, the content of Mn is made 0.30 to 3.00% The content of Mn is preferably 0.40% or more, 0.50% or more, or 0.60% or more. Further, the content of Mn is preferably 2.80% or less or 2.00%, more preferably 1.50% or less, 1.20% or less, or 0.90% or less.

P: 0.050% or less

P is an element causing a deterioration of toughness or hydrogen embrittlement resistance of the coated steel member after hardening. In particular, if the content of P is over 0.050%, the deterioration of toughness or hydrogen embrittlement resistance becomes remarkable. Therefore, the content of P is limited to 0.050% or less. The content of P is preferably limited to 0.020% or less, 0.010% or less, or 0.005% or less. The lower limit of the content of P is 0%. For reducing the refining costs, the lower limit of the content of P may be made 0.0001% or 0.001%.

S: 0.0100% or less

S is an element causing a deterioration of toughness or hydrogen embrittlement resistance of the coated steel member after hardening. In particular, if the content of S is over 0.0100%, the deterioration of toughness or hydrogen embrittlement resistance becomes remarkable. Therefore, the content of S is limited to 0.0100% or less. The content of S is preferably limited to 0.0070% or less or 0.0050% or less. The lower limit of the content of S is 0%. For reducing the steelmaking costs for reducing the content of S, the lower limit of the content of S may be made 0.0001% or 0.0005%.

N: 0.010% or less

N is an element causing a deterioration of toughness of the coated steel member after hardening. In particular, if the content of N is over 0.010%, coarse nitrides are formed in the steel and the toughness remarkably deteriorates. Therefore, the content of N is made 0.010% or less. The lower limit of the content of N is 0%. Reducing the content of N to less than 0.0002% invites an increase in steelmaking costs and is not economically preferable, so the content of N is preferably made 0.0002% or more, more preferably 0.0008% or more.

Ti: 0.010 to 0.100%

Ti is an element having the action of suppressing recrystallization when heating steel sheet to the Ac₃ point or more in temperature to heat treat it and of forming fine carbides to suppress grain growth and thereby make the austenite grains finer. For this reason, by including Ti, the effect is obtained of the toughness of the steel member greatly being improved. Further, Ti bonds with the N in the steel with priority to thereby suppress the consumption of B by precipitation of BN and promotes the effect of improvement of hardenability due to B explained later. With a content of Ti of less than 0.010%, the above effect is not sufficiently obtained. Therefore, the content of Ti is made 0.010% or more. On the other hand, if the content of Ti is over 0.100%, the amount of precipitation of TiC increases and C is consumed, so the strength of the coated steel member after hardening falls. Therefore, the content of Ti is made 0.100% or less. The content of Ti is preferably 0.015% or more or 0.025% or more and preferably 0.0800% or less or 0.045% or less.

B: 0.0005 to 0.0100%

B, even in fine amounts, has the action of dramatically raising the hardenability of steel, so is an important element in the present invention. Further, B precipitates at the grain boundaries to thereby strengthen the grain boundaries and improve the toughness and hydrogen embrittlement resistance. Furthermore, B suppresses grain growth of austenite at the time of heating the steel sheet. With a content of B of less than 0.0005%, the above effect sometimes cannot be sufficiently obtained. Therefore, the content of B is made 0.0005% or more. On the other hand, if the content of B is over 0.0100%, coarse compounds precipitate in large amounts and the toughness or hydrogen embrittlement resistance of the steel member deteriorates. Therefore, the content of B is made 0.0100% or less. The content of B is preferably 0.0010% or more, 0.0015% or more, or 0.0020% or more and preferably 0.0050% or less or 0.0030% or less.

Mo: 0.10 to 1.00%

Mo is an element which is extremely effective for raising the hardenability of steel sheet and stably securing the strength after hardening. Further, Mo segregates at the grain boundaries to thereby strengthen the grain boundaries and improve the toughness or hydrogen embrittlement resistance. Further, it has the effect of diffusing in the Al—Fe-based coating to raise the corrosion resistance. However, if the content of Mo is less than 0.10%, this effect is not sufficiently obtained. On the other hand, if the content of Mo is over 1.00%, the above effect becomes saturated and the economicalness falls. Further, Mo has the action of stabilizing the iron carbides, so if the content of Mo is over 1.00%, coarse iron carbides remain without being melted at the time of heating the steel sheet and the toughness of the steel member after hardening deteriorates. Therefore, the content of Mo if included is made 1.0% or less. The content of Mo is preferably 0.15% or more or 0.19% or more and is preferably 0.80% or less, 0.50% or less, or 0.30% or less.

Cu: 0.01 to 1.00%

Cu greatly improves the corrosion resistance in a corrosive environment in an Al—Fe-based coating and prevents hydrogen embrittlement cracking, so is an extremely important element in the present invention. However, it need not be included in the part of the steel sheet other than the coating. If Cu is contained in the steel, it diffuses to the Al—Fe-based coating and improves the corrosion resistance. Further, it is an element able to raise the hardenability of steel and stably secure the strength of the steel member after hardening. To obtain this effect, the content of Cu is preferably made 0.15% or more. On the other hand, if the content of Cu is over 1.00%, that effect becomes saturated and furthermore deterioration of the toughness or hydrogen embrittlement resistance of the coated steel member after hardening is invited. The content of Cu is preferably 0.18% or more or 0.20% or more. Further, the content of Cu is preferably 0.80% or less, 0.50% or less, or 0.35% or less.

The coated steel member of the present embodiment may further be made to include, in addition to the above elements, one or more elements selected from Cr, Ni, V, Ca, Al, Nb, Sn, W, Sb, and REMs shown below in order to raise the strength, toughness, and deoxidizing property. Further, these elements need not be included either. The lower limits of the contents of these elements are all 0%.

Cr: 0 to 1.00%

Cr is an element able to raise the hardenability of steel and stably secure the strength of the steel member after hardening, so may be included. Further, it has the effect of diffusing in the Al—Fe-based coating to improve the corrosion resistance. However, if the content of Cr is over 1.00%, that effect becomes saturated and an increase in costs is needlessly invited. Further, Cr has the action of stabilizing the iron carbides, so if the content of Cr is over 1.00%, coarse iron carbides remain without being melted at the time of heating the steel sheet and the toughness of the coated steel member after hardening deteriorates. Therefore, the content of Cr if included is made 1.00% or less. The content of Cr is preferably 0.80% or less or 0.50% or less. To obtain the above effect, the content of Cr is more preferably 0.01% or more or 0.05% or more. If the above effect does not have to be obtained, it may be made 0.05% or less or 0.01% or less.

Ni: 0 to 1.00%

Ni is an element which raises the hardenability of steel and stably secures the strength of the steel member after hardening, so may be included. Further, it has the effect of diffusing in the Al—Fe-based coating to improve the corrosion resistance. However, if the content of Ni is over 1.00%, the above effect becomes saturated and the economicalness falls. Therefore, the content of Ni if included is made 1.00% or less. The content of Ni may be made 0.80% or less or 0.50% or less. To obtain the above effect, Ni is preferably contained in 0.01% or more, more preferably is contained in 0.10% or more.

V: 0 to 1.00%

V is an element able to form fine carbides and raise the toughness due to the grain refining effect, so may be included. However, if the content of V is over 1.00%, the above effect becomes saturated and the economicalness falls. Therefore, the content of V if included is made 1.00% or less. To obtain the above effect, V is preferably included in 0.01% or more, more preferably is included in 0.10% or more. If the above effect does not have to be obtained, it may be made 0.10% or less or 0.01% or less.

Ca: 0 to 0.010%

Ca is an element which has the effect of refining inclusions in the steel and improving the toughness after hardening, so may be included. However, if the content of Ca is over 0.010%, that effect is saturated and an increase in costs is needlessly invited. Therefore, if containing Ca, the content is made 0.010% or less. The content of Ca is preferably 0.005% or less, more preferably 0.004% or less. If desiring to obtain the above effect, the content of Ca is preferably made 0.001% or more, more preferably is made 0.002% or more. If the above effect does not have to be obtained, it may be made 0.002% or less or 0.001% or less.

Al: 0 to 1.00%

Al is generally used as a deoxidizer of steel, so may be included. However, if the content of Al (however, not content of sol-Al, but content of T-Al) is over 1.00%, the above effect becomes saturated and the economicalness falls. Therefore, the content of Al if included is made 1.00% or less. The content of Al may be 0.10% or less or 0.05% or less. To obtain the above effect, Al is preferably included in 0.01% or more. If the above effect does not have to be obtained, it may be made 0.01% or less.

Nb: 0 to 0.10%

Nb is an element able to form fine carbides and raise the toughness due to the grain refining effect, so may be included. However, if the content of Nb is over 0.10%, the above effect becomes saturated and the economicalness falls. Therefore, the content of Nb if included is made 0.10% or less. The content of Nb may also be made 0.06% or less or 0.04% or less. To obtain the above effect, Nb is preferably included in 0.01% or more. If the above effect does not have to be obtained, it may be made 0.01% or less.

Sn: 0 to 1.00%

Sn improves the corrosion resistance in a corrosive environment, so may be included. However, if the content of Sn is over 1.00%, the intergranular strength falls and the toughness of the coated steel member after hardening deteriorates. Therefore, the content of Sn if included is made 1.00% or less. The content of Sn may be made 0.50% or less, 0.10%, or 0.04% or less. To obtain the above effect, Sn is preferably contained in 0.01% or more. If the above effect does not have to be obtained, it may be made 0.01% or less.

W: 0 to 1.00%

W is an element which raises the hardenability of steel and stably secures the strength of the coated steel member after hardening, so may be included. Further, W improves the corrosion resistance in a corrosive environment. However, if the content of W is over 1.00%, the above effect becomes saturated and the economicalness falls. Therefore, the content of W if included is made 1.00% or less. The content of W may be made 0.50% or less, 0.10%, or 0.04% or less. To obtain the above effect, W is preferably contained in 0.01% or more. If the above effect does not have to be obtained, it may be made 0.01% or less.

Sb: 0 to 1.00%

Sb improves the corrosion resistance in a corrosive environment, so may be included. However, if the content of Sb is over 1.00%, the intergranular strength falls and the toughness of the coated steel member after hardening deteriorates. Therefore, the content of Sb if included is made 1.00% or less. The content of Sn may also be made 0.50% or less or 0.10% or 0.04% or less. To obtain the above effect, Sb is preferably contained in 0.01% or more. If the above effect does not have to be obtained, it may be made 0.01% or less.

REMs: 0 to 0.30%

REMs are elements having the effect, like Ca, of refining inclusions in the steel and improving the toughness of the coated steel member after hardening, so may be included. However, if the content of REMs is over 0.30%, that effect becomes saturated and an increase in costs is needlessly invited. Therefore, the content of REMs if included is made 0.30% or less. The content of REMs is preferably 0.20% or less or 0.05% or less. If desiring to obtain the above effect, the content of REMs is preferably made 0.01% or more, more preferably is made 0.02% or more. If the above effect does not have to be obtained, it may be made 0.01% or less or 0.0010% or less.

Here, “REMs” indicates a total of 17 elements including Sc, Y, La, Nd, and other lanthanoids. The above “content of REMs” means the total content of these elements. REMs are added to the molten steel for example using Fe—Si-REM alloys. The alloys contain for example La, Nd, Ce, and Pr.

In the chemical compositions of the coated steel member of the present embodiment, the remainders other than the elements explained above, that is, the balances, are comprised of Fe and impurities.

Here, “impurities” mean constituents which enter from the ore, scraps, and other raw materials and various factors in the manufacturing process when industrially manufacturing steel sheet and are allowable in a range not having a detrimental effect on the present invention.

(A3) Structure of Heat Treated Coated Steel Member

The structure present in the coated steel member according to the present embodiment is a structure mainly comprised of high strength martensite. 70% or more by area ratio is martensite. Preferably, the content is 80% or more, more preferably 90% or more.

As the balance, retained austenite, bainite, ferrite, and pearlite may be included. Note that, the above-mentioned martensite also includes tempered or auto-tempered martensite. Auto-tempered martensite is martensite formed during the cooling at the time of hardening without performing heat treatment for tempering and is formed by the martensite formed being tempered on the spot by the heat generated along with martensite transformation.

(A4) Properties of Steel Member

The coated steel member of the present embodiment can be given excellent hydrogen embrittlement resistance in a corrosive environment due to the effect of corrosion resistance of the Al—Fe-based coating containing Cu and one or more of Mo, Ni, Mn, and Cr in a total by mass % of 0.12% or more so as to satisfy the above formula (1) on its surface.

Further, the coated steel member according to the present embodiment desirably not only has hydrogen embrittlement resistance in a corrosive environment, but also has a high strength of a tensile strength over 1500 MPa.

In the present embodiment, the hydrogen embrittlement resistance in a corrosive environment is evaluated by an exposure test in an actual environment of the coated steel member or an accelerated corrosion test using CCT (cyclic corrosion test). As the accelerated corrosion test, for example, the coated steel member is bent while supported at four points, subjected to a CCT based on the neutral salt spray cyclic test method described in JIS H 8502: 1999, and evaluated by the limit number of cycles where hydrogen embrittlement cracking does not occur.

Above, the coated steel member according to the present embodiment was explained, but the shape of the coated steel member is not particularly limited. That is, it may be a flat sheet, but in particular hot shaped coated steel members are in many cases shaped articles. In the present embodiment, both the case of a shaped member and the case of a flat sheet will be referred to together as a “coated steel member”. The thickness of the coated steel member does not particularly have to be prescribed, but may be 0.5 to 5.0 mm. The upper limit of the thickness may be made 4.0 mm or 3.2 mm while the lower limit may be made 0.8 mm or 1.0 mm. The tensile strength of the steel member may be made over 1500 MPa, but if necessary many also be made 1700 MPa or more, 1800 MPa or more, or 1900 MPa or more. The upper limit of the tensile strength does not particularly have to be prescribed, but may be 2500 MPa or less or 2300 MPa or less.

(B) Coated Steel Sheet

Next, the coated steel sheet will be explained.

(B1) Chemical Composition of Coated Steel Sheet

The chemical composition of the steel sheet forming the coated steel sheet (however, in the case of the later explained Morphology Y, the base sheet before formation of the intermediate layer, while in the case of the later explained Morphology Z, the base sheet before formation of the Al-based coating) is the same as the chemical composition of the coated steel member explained above. The reasons for limitation are also similar.

(B2) Content of Cu and Coating of Surface of Steel Sheet

The coated steel sheet according to the present embodiment has a layer containing Cu on the surface of the steel sheet. As specific embodiments, the following three morphologies are preferable. Similar effects can be obtained in each of the morphologies.

(B2X) Morphology X

The coated steel sheet according to the present embodiment has, as the layer containing Cu, a layer where Cu is concentrated on the surface of the steel sheet and has, on top of that, an Al-based coating.

In addition to the Fe of the main constituent of the steel sheet, the Cu concentrated at the surface of the steel sheet diffuses in the Al-based coating to form an Al—Fe-based coating containing Cu and other corrosion resistance elements in the later explained heat treatment to thereby have the effect of suppressing production of hydrogen accompanying corrosion and improving the hydrogen embrittlement resistance in a corrosive environment. If the “degree of Cu surface concentration”, defined as the ratio between the maximum value of the content of Cu in a range of a depth of 0 to 30 μm from the surface of the steel sheet and the average content of Cu at a depth of 200 μm from the surface of the steel sheet, is 1.2 or more, the concentration of corrosion resistance elements of the coated steel member becomes sufficiently high and the risk of hydrogen embrittlement accompanying corrosion becomes lower, so this is preferable. The degree of Cu surface concentration is more preferably 1.4 or more. The upper limit of the surface concentration of Cu does not have to be prescribed, but may be 2.5 or 2.1.

The surface concentration of Cu is found as follows:

GDS (glow discharge optical emission spectrometry) is performed in the thickness direction from the surface of the Al-based coated steel member to detect the content of Cu. At this time, GDS is performed from the surface of the steel member and the position of the depth where the content of Fe becomes 90% is found. The value of the maximum value of the content of Cu in a range of a depth of 0 to 30 μm from the position where the content of Fe becomes 90% divided by the content of Cu at the position of a depth of 200 μm from the position where the content of Fe becomes 90% is calculated. That value is defined as the surface concentration of Cu.

Note that, GDS is used to measure the maximum value of the content of Cu in a range of a depth of 0 to 30 μm from the position where the content of Fe becomes 90% at five random positions at a position near ¼ of the sheet width from an end of the steel member in the width direction and the content of Cu at a position of a depth of 200 μm from the position where the content of Fe becomes 90% to calculate the surface concentration of Cu. The surface concentration of Cu at the present invention is made the average value of the surface concentration of Cu at these five positions.

The coated steel sheet according to the present invention is comprised of a steel sheet having a layer where Cu is concentrated as explained above and further having an Al-based coating on its surface. By applying the later explained heat treatment to such a coated steel sheet, it is possible to obtain a coated steel member having an Al—Fe-based coating with a concentration of corrosion resistance elements of 0.12% or more and excellent in hydrogen embrittlement resistance in a corrosive environment. Note that, the “Al-based coating” is a coating which is mainly comprised of Al and preferably contains Al in 60% or more. The “coating” of the Al-based coating also can mean a film or plating layer. In general, Si is often included in 10% or so. Further, as the additive elements, there may be Mg, Ti, Zn, Sb, Sn, Cu, Co, In, Bi, Ca, Sr, a mischmetal, etc. These can be applied so long as the coating layer is mainly comprised of Al. The thickness of the Al-based coating is preferably 10 to 100 μm.

As one example of the chemical composition of the Al-based coating in the coated steel sheet (however, average chemical composition of Al-based coating as a whole), except for the case of application of the later explained Morphology Z in addition to the present embodiment, the following can be mentioned.

The chemical composition of the Al-based coating may be made, by mass %, Cu: 0 to less than 1.0%, Mo: 0 to less than 1.0%, Ni: 0 to less than 1.0%, Mn: 0 to less than 1.0%, Cr: 0 to less than 1.0%, Si: 0 to 20.0%, Al: 5.0 to 90.0%, Fe: 0 to 90%, and a balance: impurities (however, Cu+Mo+Ni+Mn+Cr: 0 to less than 1.0% and Al+Fe: 79.0% or more). Here, the lower limit of the content of Al may be made 40%, 50%, or 60%.

If the layer containing Cu is a layer where Cu is concentrated on the surface of the steel sheet, further, the average crystal grain size of the metallic structure of the steel sheet is made 30 μm or less.

The crystal grain boundaries function as paths for diffusion, so refinement of the crystal grain size results in the number of diffusion paths per unit volume increasing and as a result the actual diffusion rate becoming large, so there is the effect of further promoting the diffusion of Cu and other corrosion resistance elements into the Al-based coating in the later explained heat treatment. Therefore, refining the crystal grain size is necessary. In the morphology where the layer containing Cu is the layer where Cu is concentrated at the surface of the steel sheet, if the average crystal grain size of the steel sheet is over 30 μm, the concentration of the corrosion resistance elements of the coated steel member becomes less than 0.12% and the risk of hydrogen embrittlement accompanying corrosion rises. Therefore, the average crystal grain size of the steel sheet is made 30 μm or less. Preferably, it is 25 μm or less. The lower limit does not particularly have to be prescribed, but may be made 8 μm or 15 μm.

The average crystal grain size of the coated steel sheet is found as follows based on JIS G 0551: 2013.

A cross-section of a width (¼) part is cut out from an end of the steel sheet in the width direction so that it is parallel to the rolling direction and parallel to the thickness direction. The cross-section is polished to a mirror finish, then treated by a Nital corrosive solution to reveal the crystal grain boundaries of the ferrite. On a field enlarged using an optical microscope or a photograph taken by the same, three test lines are drawn at equal intervals in the vertical direction and three in the horizontal direction and the average line segment length per crystal grain is found. Note that, the magnification of the microscope is selected so that at least 10 or more crystal grains are caught by one test line and five random fields are examined from positions of ¼ or so of the thickness away from the surface of the steel sheet. Here, based on Appendix C.2.1 of JIS G 0551: 2013, if a test line passes through a crystal grain, the number of crystal grains caught is made 1 for that crystal, while if a test line ends inside a crystal grain or if a test line is contiguous with a crystal grain, the number of crystal grains caught is made 0.5. The average line segment length in each field is found and the average of the average line segment lengths of five fields for each of three test lines (total 15 average line segment lengths) is made the average crystal grain size.

Further, the structure present in the present embodiment is comprised of ferrite or pearlite. In the conditions of the method of manufacture explained later, bainite, martensite, and retained austenite are sometimes included. Note that, the above-mentioned martensite includes tempered and auto-tempered martensite. Auto-tempered martensite is tempered martensite formed during the cooling at the time of hardening without performing heat treatment for tempering and is formed by the martensite formed being tempered on the spot by the heat generated along with martensite transformation. The thickness of the coated steel sheet does not particularly have to be prescribed, but may be 0.5 to 5.0 mm. The upper limit of the thickness may be made 4.0 mm or 3.2 mm and the lower limit may be made 0.8 mm or 1.0 mm.

(B2Y) Morphology Y

The coated steel sheet according to the present embodiment has, as the layer containing Cu, an intermediate layer containing Cu and one or more of Mo, Ni, Mn, and Cr in a total by mass % of 30% or more on the surface of the steel sheet and further has, on top of that intermediate layer, an Al-based coating. By applying the later explained heat treatment to such a coated steel sheet, Fe of the main constituent of the steel sheet diffuses into the Al-based coating, an Al—Fe-based coating with a concentration of corrosion resistance elements of 0.12% or more is formed, and a coated steel member excellent in hydrogen embrittlement resistance in a corrosive environment can be obtained. Note that, as the base sheet of the steel sheet according to the present embodiment (base sheet before intermediate layer is formed), in addition to the steel sheet of the Morphology X, a steel sheet other than the Morphology X (so-called ordinary steel sheet) can be used.

If an intermediate layer having Cu and one or more of Mo, Ni, Mn, and Cr in a total of 30% or more at the interface of the steel sheet and the Al-based coating, the concentration of corrosion resistance elements of the coated steel member becomes sufficiently high and the risk of hydrogen embrittlement accompanying corrosion becomes lower, so this is preferable. The thickness of the intermediate layer is preferably 5 to 50 μm.

The chemical composition of the intermediate layer in the coated steel sheet (however, the average of the intermediate layer) may, for example, also comprise, by mass %, Cu: 15.0 to 20.0%, Mo: 0 to 20.0%, Ni: 0 to 20.0%, Mn: 0 to 20.0%, Cr: 0 to 20.0%, Si: 0 to 20%, Al: 0 to 60.0%, Fe: 0 to 90.0%, and a balance: impurities, where Cu+Mo+Ni+Mn+Cr: 30.0% or more.

As an example of the chemical composition of the Al-based coating in the coated steel sheet (however, average chemical composition of Al-based coating as a whole), except for the case of application of the later explained Morphology Z in addition to the present embodiment, the following can be mentioned.

The chemical composition of the Al-based coating may be made, by mass %, Cu: 0 to less than 1.0%, Mo: 0 to less than 1.0%, Ni: 0 to less than 1.0%, Mn: 0 to less than 1.0%, Cr: 0 to less than 1.0%, Si: 0 to 20.0%, Al: 5.0 to 90.0%, Fe: 0 to 90%, and a balance: impurities (however, Cu+Mo+Ni+Mn+Cr: 0 to less than 1.0% and Al+Fe: 79.0% or more). Here, the lower limit of the content of Al may be made 40%, 50%, or 60%.

(B2Z) Morphology Z

The coated steel sheet according to the present embodiment has, as the layer containing Cu, an Al-based coating containing Cu and one or more of Mo, Ni, Mn, and Cr in a total by mass % of 1.0% or more on the surface of the steel sheet. By applying the later explained heat treatment to such a coated steel sheet, Fe of the main constituent of the steel sheet diffuses into the Al-based coating, an Al—Fe-based coating with a concentration of corrosion resistance elements of 0.12% or more is formed, and a coated steel member excellent in hydrogen embrittlement resistance in a corrosive environment can be obtained. If the corrosion resistance elements in the Al-based coating become a total of 1.0% or more, the concentration of corrosion resistance elements of the coated steel member becomes sufficiently high and the risk of hydrogen embrittlement accompanying corrosion becomes lower, so this is preferable. Note that, as the base sheet of the steel sheet according to the present embodiment, in addition to the steel sheets of the Morphology X and Morphology Y, steel sheets other than the Morphology X or Morphology Y (so-called ordinary steel sheet) can be used.

As one example of the chemical composition of the Al-based coating in the coated steel sheet (however, average chemical composition of Al-based coating as a whole), the following can be mentioned.

The chemical composition of the Al-based coating may be made, by mass %, Cu: 0.1 to 20.0%, Mo: 0 to 10.0%, Ni: 0 to 10.0%, Mn: 0 to 10.0%, Cr: 0 to 10.0%, Si: 0 to 20.0%, Al: 5.0 to 90.0%, Fe: 0 to 90%, and a balance: impurities (where, Cu+Mo+Ni+Mn+Cr: 1.0% or more, Al+Fe: 70.0% or more). Here, the lower limit of the content of Al may be made 40%, 50%, or 60%.

Note that, in the case of this Morphology Z, as the steel sheet before formation of the Al-based coating with corrosion resistance elements in 1.0% or more, if using steel sheet other than the steel sheet of the above-mentioned Morphology X or Morphology Y, sometimes the ratio of the maximum value and minimum value of the content of Cu in the thickness direction cannot be made 1.4 or more in the Al—Fe-based coating.

Next, a method for manufacturing coated steel sheet will be explained.

(C) Method for Manufacturing Coated Steel Sheet

The coated steel sheet according to the present embodiment can be manufactured by using the method of manufacture shown below.

Steel having the above-mentioned chemical composition is melted in a furnace and cast, then the obtained slab is heated to 1100 to 1350° C. and hot rolled. In the hot rolling process, it is rough rolled, then descaled according to need and finally is finish rolled.

If, as in the above Morphology X, forming a concentrated layer of Cu at the surface of the steel sheet, the slab heating temperature before starting the hot rolling is made 1100 to 1350° C. If this temperature is over 1350° C., the austenite grain size during the heating becomes larger and sometimes the average crystal grain size of the steel sheet obtained after rolling exceeds 30 μm. On the other hand, if this temperature is 1100° C. or less, the alloying elements will not become sufficiently uniform and sometimes the toughness or hydrogen embrittlement resistance after the later explained heat treatment will deteriorate.

Further, if forming a concentrated layer of Cu at the surface of the steel sheet, the following parameter S₁ comprised of the time t₁ (hr) from the end of rough rolling to the start of finish rolling and the average temperature T₁ (° C.) of the rough bar during that is made 20000 or more. Here, if performing descaling after rough rolling, “the time from the end of rough rolling to the start of finish rolling” means the time until the start of finish rolling after the end of descaling.

S ₁=(T ₁+273)×(log t ₁+20)

Cu is an element which is difficult to oxidize, so elements other than Cu are oxidized with priority in the hot rolling process whereby the Cu concentrates at the surface. In particular, if making the parameter S₁ comprised of the time t₁ (hr) from the end of rough rolling to the start of finish rolling and the average temperature T₁ (° C.) of the rough bar during that 20000 or more from the end of rough rolling to the start of finish rolling, it becomes possible to make the Cu concentrate 1.2 times or more at the surface of the steel sheet. If the parameter S₁ is less than 20000, the steel sheet insufficiently oxidizes and sometimes the degree of surface concentration of Cu becomes less than 1.2. The upper limit of the above parameter S 1 is not particularly prescribed, but if over 30000, sometimes a tremendous amount of scale forms due to the oxidation and the yield falls.

If not forming a concentrated layer of Cu at the surface of the steel sheet like in the above-mentioned Morphology Y and Morphology Z, there is no need to limit the S₁ to the above-mentioned range. A general method may be used for hot rolling.

Finish rolling end temperature: Ar₃ point to 1000° C.

The end temperature of the finish rolling is made the Ar₃ point to 1000° C. If the finish rolling end temperature is over 1000° C., recrystallization of austenite occurs right after rolling and the number of nucleation sites of ferrite is limited, so the average crystal grain size of the steel sheet obtained by rolling sometimes exceeds 30 μm. On the other hand, if the finish temperature is less than the Ar₃ point, the rolling is performed after ferrite transformation and abnormal grain growth of the ferrite is invited, so the average crystal grain size of the steel sheet obtained after rolling sometimes exceeds 30 μm.

Average cooling rate from completion of finish rolling to coiling: 10° C./s or more

The average cooling rate from completion of finish rolling to coiling is made 10° C./s or more. If this average cooling rate is less than 10° C./s, the ferrite grains proceed to grow and sometimes the average crystal grain size after rolling exceeds 30 μm. The upper limit of this cooling rate is not particularly prescribed, but if over 150° C./s, the steel sheet is coiled without the ferrite transformation being completed. The transformation proceeds even after coiling, so sometimes the coil deforms due to the transformation strain.

Coiling temperature: 700° C. or less

The coiling temperature is made 700° C. or less. If this temperature is over 700° C., the ferrite grains proceed to grow and sometimes the average crystal grain size of the steel sheet after rolling exceeds 30 μm. The lower limit of this temperature is not particularly prescribed, but if falling below 500° C., martensite or bainite transformation occurs after coiling, so sometimes the coil deforms due to the transformation strain.

After the hot rolling, if necessary, descaling is performed and then cold rolling. At this time, from the viewpoint of securing good flatness, the rolling reduction in the cold rolling is preferably made 30% or more. On the other hand, to avoid the load from becoming excessively large, the rolling reduction in the cold rolling is preferably made 80% or less.

If, like in the above-mentioned Morphology X, forming a concentrated layer of Cu on the surface of the steel sheet, the hot rolled steel sheet is descaled. The descaling is made lighter pickling compared with the pickling of usual steel sheet and removes only the iron scale by hydrochloric acid or sulfuric acid pickling. Specifically, when using hydrochloric acid or sulfuric acid, making the pickling temperature 80 to 90° C., designating the acid concentration as α (%), and designating the pickling time as “t” (s), preferably 6≤α<14, 0<t≤420−30×α.

FIG. 1 shows the preferable pickling conditions (relationship of acid concentration and pickling time). For example, it is possible to use concentration 12% hydrochloric acid for descaling for an immersion time of 30 seconds to remove only the iron scale and leave the Cu concentrated layer of the surface of the steel sheet obtained in the above hot rolling process.

If manufacturing the Al-based coated steel sheet of the present embodiment, the hot rolled steel sheet or cold rolled steel sheet is annealed. In the annealing process, the hot rolled steel sheet or cold rolled steel sheet is annealed in for example the 550 to 950° C. temperature region.

The method of the Al-based coating is not particularly limited. Hot dip coating first and foremost and also electroplating, vacuum deposition, cladding, etc. are possible. Al thermal spraying may also be used to form an Al thermal sprayed layer. The most popular method industrially is hot dip coating. As the usual coating bath, Al-10% Si is often used. Fe is mixed in this as an impurity.

If like in the above-mentioned Morphology Z, making the layer containing Cu an Al-based coating, the Al-based coating is performed by an Al coating bath containing, in addition to this, Cu and one or more of Mo, Ni, Mn, and Cr in a total by mass % of 1.0% or more.

Further, as elements which can be added to the coating bath besides the above-mentioned elements, there are Mg, Ti, Zn, Sb, Sn, Cu, Co, In, Bi, Ca, Sr, a mischmetal, etc. These elements can also be used so long as the coating layer is mainly comprised of Al.

The pretreatment and post treatment of the Al-based coating are not particularly limited. Precoating or solvent coating, alloying, etc. are possible.

If like in the above-mentioned Morphology Y, making the layer containing Cu an intermediate layer, before coating, the surface of the steel sheet is precoated with an intermediate layer containing Cu and one or more of Mo, Ni, Mn, and Cr in a total by mass % of 30% or more. The precoating can be performed by electroplating or thermal spraying etc.

By applying the later explained heat treatment to the coated steel sheet manufactured in this way, it becomes possible to obtain a coated steel member excellent in hydrogen embrittlement resistance in a corrosive environment which has a concentration of corrosion resistance elements at an Al—Fe coating of 0.12% or more.

(D) Method for Manufacturing Coated Steel Member

Next, the method for manufacturing a coated steel member according to the present embodiment will be explained.

In the method for manufacturing a coated steel member of the present embodiment, a coated steel sheet comprised of a steel sheet having the above-mentioned chemical composition and having a metallic structure with a surface concentration of Cu within a depth of 30 μm from the surface of 1.2 or more and with an average crystal grain size of 30 μm or less on the surface of which an Al-based coating is provided, a coated steel sheet comprised of a steel sheet on the surface of which an intermediate layer containing Cu and one or more of Mo, Ni, Mn, and Cr in a total by mass % of 30% or more is provided and on which layer an Al-based coating is provided, or a coated steel sheet comprised of a steel sheet on the surface of which an Al-based coating containing Cu and one or more of Mo, Ni, Mn, and Cr in a total by mass % of 1.0% or more is provided can be treated by the heat treatment shown below to thereby obtain a coated steel member excellent in hydrogen embrittlement resistance in a corrosive environment characterized by having a concentration of corrosion resistance elements in the Al—Fe coating of 0.12% or more.

The average rate of temperature rise explained below is made the value of the amount of temperature rise of the steel sheet from the time of start of heating to the time of end of heating divided by the time required from the time of start of heating to the time of end of heating.

Further, the average cooling rate is made the value of the amount of temperature fall from the time of start of cooling to the time of end of cooling divided by the time required from the time of start of cooling to the time of end of cooling.

The above-mentioned steel sheet is heated by a 5 to 1000° C./s average rate of temperature rise up to T₂ (° C.) of the temperature region of the Ac₃ point to (Ac₃ point+300°) C., is cooled down to Ms ° C. by an average cooling rate made the upper critical cooling rate or more, then cooled from the Ms point to 100° C. or less by an average cooling rate of 5° C./s or more. At the time of heating, the following parameter S₂, comprised of the peak heating temperature T₂ (° C.) and the time t₂ (hr) from when reaching a temperature 10° C. lower than T₂ to when ending the heating, is made 19000 or more. The features of this heat treatment will be explained below. Here, the upper critical cooling rate is the minimum cooling rate where the structure becomes 100% martensite. Various methods are known as the method for measuring this, but one example will be explained in the section on examples. Further, the time until ending the heating means the time until right before starting cooling. For example, if held for a certain time after reaching T₂ (° C.), that holding time is also included.

S ₂=(T ₂+273−10)×(log t ₂+20)

S₂ from peak heating temperature −10° C. to heating end: 19000 or more

If the above parameter comprised of the peak heating temperature T₂ (° C.) and the time t₂ (hr) from when reaching a temperature 10° C. lower than T₂ to when ending the heating is made 19000 or more, the Cu and the Mo, Ni, Mn, and Cr sufficiently diffuse in the Al-based coating and the corrosion resistance is improved. If the above parameter S₂ is less than 19000, sometimes the corrosion resistance elements insufficiently diffuse and the corrosion resistance is not sufficiently improved. The upper limit of S₂ is not particularly prescribed, but if over 30000, sometimes the productivity in the heat treatment falls.

Note that if the rate of temperature rise is less than 5° C./s, the structure becomes coarser and the hydrogen embrittlement resistance falls, so this is not preferable. On the other hand, if the rate of temperature rise is over 1000° C./s, the structure becomes a mixed grain type and the hydrogen embrittlement resistance falls, so this is not preferable.

Further, if the heating temperature is less than the Ac₃ point, a small amount of ferrite remains mixed in after the cooling and the hydrogen embrittlement resistance and strength fall, so this is not preferable. On the other hand, if the peak temperature of heating is over the (Ac₃ point+300), the structure becomes coarser and the toughness falls, so this is not preferable.

Further, if the average cooling rate from the Ms point to 100° C. or less is less than 5° C./s, the spot tempering of the martensite (auto-tempering) excessively proceeds and the strength becomes insufficient, so this is not preferable.

Here, at the time of the above series of heat treatment, it is also possible to perform hot shaping such as hot stamping while cooling to the Ms point after heating to a temperature region of the Ac₃ point to (Ac₃ point+300°) C., that is, simultaneously with the process of cooling by the upper critical cooling rate or more. As the hot shaping, bending, drawing, bulging, hole expanding, flanging, etc. may be mentioned. Further, if providing means for cooling the steel sheet simultaneously with or directly after shaping, the present invention may also be applied to a shaping method other than press forming, for example, roll forming. Note that if following the above-mentioned heat history, it is also possible to repeatedly perform hot shaping.

Note that, as explained above, in the present invention, both what is hot shaped to form a shaped article and what is only heat treated to form a flat sheet will be referred to together as “coated steel members”.

Further, it is possible to hot shape or heat treat part of the steel materials to obtain steel members having regions of different strengths.

The above series of heat treatment can be performed by any methods. For example, they may be performed by high frequency hardening, ohmic heating, infrared heating, or furnace heating.

EXAMPLES

Below, examples will be used to explain the present invention more specifically, but the present invention is not limited to these examples.

First, in manufacturing the coated steel sheet and coated steel member, steel having each of the chemical constituents shown in Table 1 and Table 2 was melted to obtain a slab for hot rolling use.

TABLE 1 Steel Chemical composition (mass %) no. C Si Mn P S N Ti B Cu Mo Cr Ni A1 0.29 0.40 0.90 0.010 0.0007 0.004 0.040 0.0025 0.21 0.19 A2 0.50 0.50 0.40 0.012 0.0005 0.003 0.032 0.0026 0.25 0.15 0.10 0.10 A3 0.30 0.30 1.00 0.011 0.0008 0.004 0.040 0.0025 0.20 0.18 A4 0.32 1.60 0.90 0.012 0.0006 0.002 0.032 0.0026 0.26 0.16 0.20 A5 0.31 0.35 0.32 0.009 0.0010 0.002 0.040 0.0025 0.21 0.20 0.15 A6 0.34 0.40 2.50 0.018 0.0010 0.002 0.032 0.0026 0.26 0.15 A7 0.36 0.55 0.95 0.030 0.0009 0.002 0.040 0.0025 0.20 0.20 A8 0.38 0.60 0.80 0.010 0.0080 0.002 0.040 0.0025 0.21 0.21 A9 0.33 0.70 0.75 0.009 0.0012 0.008 0.032 0.0026 0.21 0.20 0.23 A10 0.30 0.55 0.70 0.008 0.0010 0.003 0.020 0.0025 0.24 0.15 A11 0.36 0.63 0.65 0.012 0.0009 0.002 0.080 0.0026 0.25 0.20 0.15 A12 0.34 0.38 0.85 0.014 0.0009 0.002 0.034 0.0010 0.21 0.18 0.18 A13 0.34 0.41 0.75 0.016 0.0008 0.003 0.022 0.0060 0.27 0.20 A14 0.36 0.40 0.77 0.010 0.0010 0.004 0.040 0.0025 0.18 0.16 A15 0.37 0.45 0.80 0.008 0.0009 0.003 0.032 0.0026 0.70 0.21 0.23 A16 0.36 0.52 0.78 0.010 0.0008 0.004 0.040 0.0025 0.20 0.13 0.10 A17 0.39 0.50 0.69 0.009 0.0006 0.002 0.032 0.0026 0.28 0.70 A18 0.33 0.39 0.65 0.012 0.0008 0.004 0.040 0.0025 0.21 0.20 0.70 A19 0.31 0.40 0.55 0.008 0.0005 0.003 0.032 0.0026 0.25 0.15 0.60 A20 0.30 0.42 0.67 0.007 0.0007 0.006 0.040 0.0025 0.20 0.20 0.10 A21 0.35 0.51 0.78 0.008 0.0006 0.003 0.032 0.0026 0.24 0.15 0.23 A22 0.36 0.35 0.90 0.005 0.0008 0.005 0.040 0.0025 0.20 0.20 A23 0.40 0.63 0.75 0.010 0.0008 0.004 0.040 0.0025 0.20 0.20 0.14 A24 0.32 0.43 0.65 0.009 0.0005 0.003 0.032 0.0026 0.21 0.16 0.20 A25 0.31 0.47 0.60 0.010 0.0008 0.005 0.040 0.0025 0.24 0.19 A26 0.32 0.46 1.05 0.015 0.0005 0.003 0.032 0.0026 0.20 0.17 0.23 A27 0.36 0.52 0.90 0.016 0.0009 0.003 0.026 0.0026 0.24 0.19 0.15 A28 0.30 0.40 0.90 0.010 0.0008 0.004 0.040 0.0025 0.20 0.20 A29 0.35 0.50 0.75 0.008 0.0005 0.003 0.032 0.0026 0.25 0.15 0.10 0.15 A30 0.35 0.50 0.40 0.009 0.0008 0.004 0.021 0.0025 0.05 0.15 0.20 A31 0.37 0.45 0.45 0.010 0.0009 0.004 0.025 0.0020 0.10 0.12 0.10 Upper critical Transformation cooling Steel Chemical composition (mass %) point (° C.) rate no. V Ca Al Nb Sn W Sb REM Ar3 Ac3 Ms (° C./s) A1 793 826 396 20 A2 0.04 0.04 774 808 326 20 A3 781 815 388 20 A4 0.10 860 895 370 10 A5 0.01 0.20 801 831 409 40 A6 0.25 0.004 744 775 312 10 A7 0.02 0.18 809 834 361 20 A8 0.06 0.15 805 834 361 20 A9 0.30 804 836 377 20 A10 0.15 0.15 793 829 396 30 A11 0.003 816 849 368 20 A12 779 812 377 20 A13 0.03 0.24 785 818 378 20 A14 0.25 0.30 787 815 371 20 A15 0.03 0.26 768 795 356 20 A16 0.26 793 819 372 20 A17 0.003 0.18 799 832 349 10 A18 0.05 0.25 789 826 372 10 A19 0.002 0.15 781 818 396 30 A20 0.70 0.05 0.20 798 829 398 30 A21 0.008 0.15 782 815 375 20 A22 0.10 0.70 0.27 852 882 367 20 A23 0.07 792 826 350 20 A24 0.60 0.15 793 824 390 30 A25 0.002 0.70 806 833 397 30 A26 0.03 0.60 789 815 373 20 A27 0.002 0.16 0.20 783 817 364 20 A28 0.16 792 826 389 20 A29 0.04 0.04 785 817 370 20 A30 0.05 0.03 0.36 793 825 390 40 A31 0.05 0.05 0.10 790 822 380 30

TABLE 2 Chemical composition (mass %) Steel no. C Si Mn P S N Ti B Cu Mo Cr Ni V a1 0.17 0.40 0.85 0.010 0.0008 0.004 0.040 0.0025 0.08 0.18 0.10 0.10 a2 0.80 0.50 0.80 0.008 0.0006 0.003 0.032 0.0026 0.10 0.16 a3 0.33 0.02 0.30 0.011 0.0008 0.004 0.040 0.0025 0.09 0.12 0.20 a4 0.45 3.00 1.50 0.007 0.0009 0.005 0.032 0.0026 0.11 0.25 0.40 0.25 a5 0.36 0.40 0.05 0.009 0.0009 0.004 0.040 0.0025 0.10 0.15 0.25 a6 0.40 0.45 5.00 0.018 0.0010 0.003 0.032 0.0026 0.11 0.21 a7 0.40 0.52 0.90 0.100 0.0009 0.002 0.040 0.0025 0.10 0.20 0.20 a8 0.43 0.47 0.80 0.010 0.1000 0.001 0.040 0.0025 0.11 0.15 0.43 0.30 a9 0.37 0.39 0.85 0.010 0.0010 0.100 0.032 0.0026 0.08 0.20 a10 0.44 0.40 0.79 0.000 0.0010 0.001 0.001 0.0025 0.10 0.17 0.15 a11 0.30 0.56 0.75 0.009 0.0008 0.006 0.300 0.0026 0.08 0.21 0.20 a12 0.34 0.45 0.69 0.008 0.0010 0.004 0.021 0.0002 0.10 0.18 0.50 a13 0.40 0.52 0.74 0.010 0.0009 0.002 0.022 0.0500 0.11 0.22 0.25 a14 0.41 0.39 1.10 0.012 0.0006 0.003 0.022 0.0026 3.00 0.20 0.40 a15 0.39 0.40 0.81 0.008 0.0008 0.006 0.021 0.0025 0.12 0.02 0.45 a16 0.39 0.66 1.00 0.007 0.0005 0.003 0.022 0.0025 0.09 3.00 0.25 a17 0.42 0.51 0.76 0.008 0.0007 0.005 0.026 0.0026 0.08 0.20 2.00 0.30 a18 0.40 0.63 0.65 0.010 0.0008 0.002 0.031 0.0031 0.10 0.22 0.30 0.50 a19 0.44 0.88 0.60 0.010 0.0008 0.002 0.031 0.0031 0.12 0.21 0.35 0.20 Transformation Upper critical Chemical composition (mass %) point (° C.) cooling rate Steel no. Ca Al Nb Sn W Sb REM Ar3 Ac3 Ms (° C./s) a1 0.002 0.04 0.04 0.30 0.40 817 847 432 30 a2 728 756 190 10 a3 0.25 769 801 401 60 a4 0.01 0.20 894 916 272 10 a5 0.004 803 830 396 70 a6 0.08 0.18 682 710 191 10 a7 0.06 0.15 844 879 347 20 a8 773 805 332 20 a9 0.30 3.00 781 809 361 20 a10 0.003 0.06 748 780 333 20 a11 893 914 390 20 a12 0.03 0.24 773 809 369 70 a13 0.30 0.45 783 811 354 20 a14 0.30 699 736 275 10 a15 0.004 0.40 0.23 768 798 359 40 a16 0.04 0.40 860 892 284 10 a17 0.08 0.40 762 797 302 10 a18 2.00 787 822 350 20 a19 0.08 2.00 806 836 333 10

Ar₃ and Ac₃ Points, Ms Point, and Upper Critical Cooling Rate

Each obtained slab was examined for the Ar₃ point, Ac₃ point, Ms point, and upper critical cooling rate by the following method. The results are shown in Table 1 and Table 2.

From the slab, a diameter 3 mm, length 10 mm columnar test piece was cut out. The test piece was heated in the air atmosphere up to 1000° C. by a 10° C./s average rate of temperature rise, was held at that temperature for 5 minutes, then was cooled down to room temperature by various cooling rates. The cooling rates were set at 10° C./s intervals from 1° C./s to 100° C./s. The changes in the thermal expansion of the test piece during the heating and cooling at that time were measured and the structure of the test piece after cooling was examined to thereby measure the Ar₃ point, Ac₃ point, Ms point, and upper critical cooling rate.

Regarding the upper critical cooling rate, the minimum cooling rate where no ferrite phases precipitated in each test piece cooled by the above cooling rates was made the upper critical cooling rate.

Next, the obtained slabs were used to prepare the coated steel sheets and coated steel members shown in the following Examples 1 to 5.

Example 1

Each slab of the above Table 1 and Table 2 was hot rolled to obtain a thickness 3.0 mm hot rolled steel sheet. In the hot rolling process, the slab heating temperature was made 1250° C. and the slab was hot rolled and pickled. Next, this was cold rolled to obtain a thickness 1.4 mm cold rolled steel sheet, then this was coated to obtain an Al-based coated steel sheet. The hot rolling, pickling, and coating conditions are shown in Tables 3 and 4. Note that, in Table 3 and Table 4, t₁ (s) is the time from the end of rough rolling to the start of finish rolling, T₁ (° C.) is the average temperature of the rough bar from the end of rough rolling to the start of finish rolling, and S₁ is the value found by (T₁+273)×(log t₁+20). However, in the formula of S₁, the unit of t₁ is (hr). Further, in the column of “hot dip Al coating”, A, B, and C respectively mean the following coating:

A: hot dip Al coating by a usual coating bath (not including corrosion resistance elements)

B: hot dip Al coating by a coating bath with a total content of corrosion resistance elements of more than 0% and less than 1.0%

C: hot dip Al coating by a coating bath with a total content of corrosion resistance elements of 1.0% or more

The above coated steel sheet was heated to the T₂ (° C.) of Tables 3 and 4 by an average rate of temperature rise of 10° C./s and held there for t₂ (s). S₂ of Tables 3 and 4 is a value found by (T₂+273−10)×(log t₂+20). However, in the formula of S₂, the unit of t₂ is (hr). Next, the coated steel sheet was cooled down to the Ms point by an average cooling rate of 50° C./s, then was cooled down to 100° C. by an average cooling rate of 30° C./s as heat treatment to obtain the coated steel member.

After that, test pieces were cut out from the coated steel member and subjected to GDS (glow discharge optical emission spectrometry), a tensile test, and CCT (salt spray cyclic corrosion test) by the following methods to evaluate the concentration of corrosion resistance elements in Al—Fe-based coating, the concentration of Si (content of Si) in the Al—Fe-based coating, the tensile strength, and critical number of cycles of CCT (hydrogen embrittlement resistance in a corrosive environment). The results of evaluation of the coated steel member are shown in Tables 5-1 to 6-2.

Concentration of Corrosion Resistance Elements and Concentration of Si in Al—Fe-Based Coating

The concentration of corrosion resistance elements and the concentration of Si in the Al—Fe-based coating were measured by the following procedure.

GDS (glow discharge optical emission spectrometry) was performed in the thickness direction from the surface of the coated steel member to find the maximum contents of Cu, Mo, Ni, Mn, Cr, and Si in the Al—Fe-based coating. The measurement by GDS was performed at five random points at a position of ¼ of the sheet width (short side) from an end of the coated steel member in the width direction, the maximum amounts of Cu, Mo, Ni, Mn, and Cr in the Al—Fe-based coating at the different points were found, and the average values of the different elements at the five points were used by the formula (1) to find the concentration of corrosion resistance elements in the Al—Fe-based coating. Note that, Al—Fe-based coating was deemed to mean the region where the content of Fe becomes less than 90% when performing GDS from the surface of the coated steel member. Note that, at the surface most layer, sometimes oxide scale and impurities are present, so the content of 0 was also measured and measurement values of the concentration of corrosion resistance elements in the range of thickness where the content of 0 is 1.0% or more were excluded.

Cu+0.01×63.5(Mo/95.9+Ni/58.7+Mn/54.9+Cr/52.0)≥0.12%  formula (1)

Tensile Strength

A tensile test was conducted based on the provisions of the ASTM Standard E8. A half size plate-shaped test piece (parallel part length: 32 mm, parallel part width: 6.25 mm) of ASTM standard E8 was taken from a soaked part of the above coated steel member so that the test direction became parallel to the rolling direction.

Further, a strain gauge (gauge length: 5 mm) was attached to each test piece and a room temperature tensile test was conducted by a strain rate of 3 mm/min to measure the tensile strength (maximum strength). Note that, in the present embodiment, cases having a tensile strength over 1500 MPa were evaluated as being excellent in strength.

Critical Number of Cycles of CCT

The CCT was performed based on the provisions of the neutral salt spray cyclic test method described in JIS H 8502: 1999. A width 8 mm, length 68 mm strip shaped test piece was prepared from a soaking part of the above coated steel member. Further, a strain gauge (gauge length: 5 mm) similar to the tensile test was attached to the center of the test piece surface in the width and length directions and was bent by a four-point support jig until a strain equivalent to ½ of the tensile strength. The test piece bent at four points was inserted in the CCT apparatus together with its jig and subjected to the CCT described in the above JIS H 8502: 1999 comprised of cycles of spraying saltwater for 2 hours, drying for 4 hours, and wetting for 2 hours. During this, the test piece was observed for 3 cycles every 24 hours and was checked for any cracking up to 360 cycles. The limit number of cycles up to which no cracking occurred was found. In the present embodiment, the test was conducted five times and cases where no hydrogen embrittlement cracking occurred up to an average 150 cycles were deemed excellent in hydrogen embrittlement resistance in a corrosive environment.

As shown in Tables 3 to 6-2, Invention Examples B1 to B45 satisfying the scope of the present invention turned out to be excellent in both of the concentration of corrosion resistance elements in the Al—Fe-based coating and the properties, but Comparative Examples b1 to b23 not satisfying the scope of the present invention turned out to not satisfy the concentration of corrosion resistance elements in the Al—Fe-based coating.

TABLE 3 Electroplating including Hot rolling Pickling corrosion Hot dip Heat treatment t1 T1 Conc. Temp. Time resistance Al T2 t2 Symbol Steel no. (s) (° C.) S1 Acid (%) (° C.) (s) elements coating (° C.) (s) S2 B1 A1 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 B2 A2 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 B3 A3 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 B4 A4 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 B5 A5 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 B6 A6 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 B7 A7 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 B8 A8 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 B9 A9 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 B10 A10 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 B11 A11 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 B12 A12 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 B13 A13 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 B14 A14 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 B15 A15 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 B16 A16 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 B17 A17 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 B18 A18 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 B19 A19 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 B20 A20 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 B21 A21 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 B22 A22 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 B23 A23 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 B24 A24 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 B25 A25 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 B26 A26 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 B27 A27 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 B28 A28 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 B29 A29 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 B30 A30 12 1020 22657 Hydrochloric 12 90 30 Yes C 920 90 21765 B31 A30 12 1020 22657 Hydrochloric 12 90 30 Yes B 920 90 21765 B32 A30 12 1020 22657 Hydrochloric 12 90 30 Yes C 920 90 21765 B33 A30 12 1020 22657 Hydrochloric 12 90 30 Yes C 920 90 21765 B34 A31 12 1020 22657 Hydrochloric 12 90 30 Yes C 920 90 21765 B35 A31 12 1020 22657 Hydrochloric 12 90 30 Yes B 920 90 21765 B36 A31 12 1020 22657 Hydrochloric 12 90 30 Yes C 920 90 21765 B37 A31 12 1020 22657 Hydrochloric 12 90 30 Yes C 920 90 21765 B38 a4 12 1020 22657 Hydrochloric 12 90 30 Yes B 920 90 21765 B39 a9 12 1020 22657 Hydrochloric 12 90 30 Yes B 920 90 21765 B40 a10 12 1020 22657 Hydrochloric 12 90 30 Yes B 920 90 21765 B41 a15 12 1020 22657 Hydrochloric 12 90 30 Yes C 920 90 21765 B42 a16 12 1020 22657 Hydrochloric 12 90 30 Yes C 920 90 21765 B43 a17 12 1020 22657 Hydrochloric 12 90 30 Yes C 920 90 21765 B44 a18 12 1020 22657 Hydrochloric 12 90 30 Yes C 920 90 21765 B45 a19 12 1020 22657 Hydrochloric 12 90 30 Yes C 920 90 21765

TABLE 4 Electroplating including Hot rolling Pickling corrosion Hot dip Heat treatment t1 T1 Conc. Temp. Time resistance Al T2 t2 Symbol Steel no. (s) (° C.) S1 Acid (%) (° C.) (s) elements coating (° C.) (s) S2 b1 a1 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 b2 a2 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 b3 a3 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 b4 a4 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 b5 a5 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 b6 a7 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 b7 a8 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 b8 a9 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 b9 a10 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 b10 a11 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 b11 a12 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 b12 a13 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 b13 A30 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 b14 A31 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 b15 a15 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 b16 a16 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 b17 a17 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 b18 a18 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 b19 a19 12 1020 22657 Hydrochloric 12 90 30 — A 920 90 21765 b20 A28 5 880 19765 Hydrochloric 12 90 30 — A 920 90 21765 b21 A29 5 880 19765 Hydrochloric 12 90 30 — A 920 90 21765 b22 A28 12 1020 22657 Sulfuric 15 80 180 — A 920 90 21765 b23 A29 12 1020 22657 Hydrochloric 12 90 90 — A 920 90 21765

TABLE 5 Table 5-1 Coated steel member Concentration of Maximum Maximum corrosion Maximum Cu Mo Maximum Ni Mn Maximum Cr resistance Maximum Si content in content in content in content in content in elements in content in Thickness Al—Fe- Al—Fe- Al—Fe- Al—Fe- Al—Fe- Al—Fe- Al—Fe- of Al—Fe- based based based based based based based based coating coating coating coating coating coating coating coating Symbol (mass %) (mass %) (mass %) (mass %) (mass %) (mass %) (mass %) (μm) Inv. ex. B1 0.18 0.18 0.00 0.83 0.00 0.19 0 40 B2 0.21 0.14 0.12 0.35 0.16 0.22 0 40 B3 0.18 0.16 0.00 0.91 0.00 0.19 0 40 B4 0.21 0.13 0.00 1.02 0.24 0.22 0 40 B5 0.19 0.19 0.17 0.29 0.00 0.19 0 40 B6 0.22 0.14 0.00 2.28 0.00 0.25 0 40 B7 0.15 0.19 0.00 0.87 0.00 0.16 0 40 B8 0.19 0.21 0.00 0.72 0.00 0.20 0 40 B9 0.18 0.17 0.00 0.66 0.29 0.19 0 60 B10 0.19 0.14 0.00 0.66 0.00 0.20 0 60 B11 0.19 0.19 0.00 0.60 0.23 0.20 0 60 B12 0.17 0.17 0.21 0.78 0.00 0.18 0 60 B13 0.23 0.18 0.00 0.68 0.00 0.24 0 60 B14 0.15 0.14 0.00 0.71 0.00 0.16 0 60 B15 0.56 0.21 0.25 0.73 0.00 0.57 0 60 B16 0.18 0.13 0.12 0.72 0.00 0.19 0 60 B17 0.23 0.64 0.00 0.63 0.00 0.25 0 60 B18 0.17 0.19 0.00 0.58 0.71 0.18 0 60 B19 0.21 0.14 0.65 0.50 0.00 0.22 0 30 B20 0.17 0.17 0.00 0.62 0.15 0.18 0 30 B21 0.21 0.13 0.27 0.69 0.00 0.22 0 30 B22 0.17 0.19 0.00 0.83 0.00 0.18 0 30 B23 0.17 0.19 0.00 0.68 0.18 0.18 0 30 B24 0.18 0.13 0.21 0.60 0.00 0.19 0 30 B25 0.19 0.15 0.00 0.56 0.00 0.20 14 30 B26 0.16 0.15 0.00 0.97 0.29 0.18 10 30 B27 0.18 0.18 0.16 0.82 0.00 0.19 11 30 B28 0.16 0.19 0.00 0.81 0.00 0.17 12 30 B29 0.21 0.14 0.17 0.67 0.16 0.22 10 30 B30 0.31 0.15 0.21 3.00 0.00 0.35 0 35 B31 0.21 2.50 0.21 0.36 0.00 0.23 0 35 B32 0.20 0.15 1.00 0.36 1.60 0.24 0 35 B33 0.10 1.20 0.80 1.50 1.20 0.15 0 35 B34 0.30 0.10 0.00 5.00 0.12 0.36 0 35 B35 0.23 2.00 0.00 0.39 0.12 0.25 0 35 B36 0.21 0.10 1.00 0.39 2.00 0.25 0 35 B37 0.11 1.50 1.20 2.00 0.80 0.17 0 35 B38 0.24 0.55 0.29 1.36 0.40 0.27 0 50 B39 0.22 0.19 1.05 0.77 0.00 0.24 0 50 B40 0.24 0.14 0.00 1.89 0.20 0.27 0 50 B41 0.24 0.03 0.00 0.72 0.00 0.25 8 50 B42 0.25 2.68 0.27 0.89 1.06 0.29 10 50 B43 0.24 0.72 0.00 0.67 1.96 0.28 8 50 B44 0.23 0.21 0.68 0.59 0.30 0.25 15 50 B45 0.25 0.19 0.22 1.32 0.34 0.27 11 50

TABLE 6 Table 5-2 Coated steel member Average Al Average Fe Minimum Cu content in Al—Fe- content in Al—Fe- content in Al—Fe- Max/min Cu Tensile based coating based coating based coating content in Al—Fe- strength CCT Symbol (mass %) (mass %) (mass %) based coating (MPa) No. of cycles Inv. ex. B1 41 58 0.10 1.8 1897 360 B2 40 59 0.12 1.8 2742 186 B3 41 58 0.10 1.8 1947 360 B4 41 58 0.11 1.9 2046 300 B5 41 58 0.11 1.7 1912 360 B6 40 59 0.12 1.8 2273 195 B7 40 59 0.07 2.1 2199 210 B8 41 58 0.11 1.7 2271 216 B9 40 59 0.10 1.8 2056 309 B10 40 59 0.10 1.9 1915 327 B11 40 59 0.10 1.9 2072 360 B12 41 58 0.09 1.9 2103 306 B13 40 59 0.12 1.9 2092 309 B14 41 58 0.09 1.7 2177 258 B15 40 59 0.29 1.9 2223 270 B16 41 58 0.10 1.8 2185 306 B17 40 59 0.13 1.8 2304 324 B18 40 59 0.09 1.9 2038 303 B19 40 59 0.12 1.8 1940 312 B20 41 58 0.09 1.9 1909 360 B21 41 58 0.12 1.8 2141 360 B22 41 58 0.09 1.9 2194 342 B23 40 59 0.09 1.9 2351 360 B24 40 59 0.10 1.8 1998 339 B25 32 58 0.10 1.9 1950 360 B26 35 58 0.08 2.0 2042 342 B27 34 58 0.09 2.0 2194 360 B28 32 59 0.08 2.0 1937 360 B29 35 58 0.12 1.8 2136 360 B30 40 59 0.17 1.8 2102 270 B31 41 58 0.09 2.3 2102 171 B32 40 59 0.14 1.4 2100 172 B33 41 58 0.06 1.7 2104 162 B34 40 59 0.17 1.8 2195 240 B35 41 58 0.10 2.3 2192 165 B36 41 58 0.14 1.5 2194 165 B37 41 58 0.07 1.6 2190 162 B38 40 59 0.11 2.2 2700 165 B39 40 59 0.10 2.2 2230 222 B40 40 59 0.12 2.0 2523 192 B41 35 59 0.16 1.5 2310 183 B42 35 58 0.17 1.5 2335 234 B43 36 58 0.16 1.5 2436 219 B44 32 58 0.15 1.5 2345 227 B45 33 59 0.17 1.5 2513 213

TABLE 7 Table 6-1 Coated steel member Concentration of Maximum Maximum corrosion Maximum Cu Mo Maximum Ni Mn Maximum Cr resistance Maximum Si Thickness content in content in content in content in content in elements in content in of Al—Fe- Al—Fe- Al—Fe- Al—Fe- Al—Fe- Al—Fe- Al—Fe- Al—Fe- based based based based based based based based coating coating coating coating coating coating coating coating Symbol (mass %) (mass %) (mass %) (mass %) (mass %) (mass %) (mass %) (μm) Comp. ex. b1 0.05 0.15 0.10 0.77 0.16 0.06 0 20 b2 0.07 0.15 0.00 0.73 0.00 0.08 0 20 b3 0.06 0.12 0.00 0.28 0.24 0.07 0 20 b4 0.07 0.23 0.29 1.36 0.40 0.10 0 20 b5 0.07 0.15 0.00 0.06 0.00 0.07 0 20 b6 0.06 0.18 0.23 0.84 0.00 0.07 0 20 b7 0.07 0.14 0.00 0.71 0.42 0.08 0 50 b8 0.06 0.19 0.00 0.77 0.00 0.07 0 50 b9 0.05 0.14 0.00 0.72 0.20 0.06 0 50 b10 0.06 0.19 0.22 0.70 0.00 0.07 0 50 b11 0.07 0.16 0.00 0.64 0.49 0.08 0 50 b12 0.06 0.21 0.00 0.68 0.00 0.07 0 50 b13 0.04 0.11 0.22 0.36 0.00 0.05 0 50 b14 0.06 0.12 0.00 0.41 0.16 0.07 0 50 b15 0.07 0.03 0.00 0.72 0.00 0.08 25 80 b16 0.05 2.68 0.27 0.89 0.00 0.08 23 80 b17 0.04 0.18 0.00 0.67 1.96 0.07 30 80 b18 0.07 0.21 0.00 0.59 0.30 0.08 32 80 b19 0.07 0.19 0.22 0.55 0.34 0.08 25 80 b20 0.08 0.15 0.00 0.61 0.00 0.09 12 30 b21 0.09 0.10 0.11 0.46 0.14 0.10 10 30 b22 0.07 0.14 0.00 0.63 0.00 0.08 12 30 b23 0.08 0.09 0.12 0.46 0.14 0.09 10 30

TABLE 8 Table 6-2 Coated steel member Average Al Average Fe Minimum Cu Al—Fe- Al—Fe- Al—Fe- Max/min Cu based based based content in Tensile coating coating coating Al—Fe- strength CCT Symbol (mass %) (mass %) (mass %) based coating (MPa) No. of cycles Comp. ex. b1 40 59 0.04 1.3 1400 189 b2 40 59 0.06 1.2 3069 21 b3 40 59 0.05 1.2 1490 177 b4 40 59 0.06 1.2 2700 48 b5 40 59 0.06 1.2 1425 180 b6 41 58 0.05 1.2 2369 60 b7 41 58 0.06 1.2 2483 42 b8 41 58 0.05 1.2 2230 108 b9 41 58 0.04 1.3 2523 75 b10 40 59 0.05 1.2 1422 180 b11 41 58 0.06 1.2 1483 177 b12 40 59 0.05 1.2 2352 60 b13 41 58 0.03 1.3 2102 54 b14 40 59 0.05 1.2 2192 51 b15 25 59 0.06 1.2 2310 69 b16 27 58 0.04 1.3 2335 117 b17 23 58 0.03 1.3 2436 108 b18 21 58 0.06 1.2 2345 110 b19 26 58 0.06 1.2 2513 99 b20 32 59 0.06 1.3 1937 126 b21 35 58 0.07 1.3 2136 102 b22 32 59 0.06 1.2 1937 120 b23 35 58 0.06 1.3 2136 99

Example 2

Each slab of the above Table 1 and Table 2 was hot rolled to obtain a thickness 3.0 mm hot rolled steel sheet. In the hot rolling process, the slab heating temperature was made 1250° C. and the slab was hot rolled and pickled to obtain hot rolled steel sheet. Table 7 shows the hot rolling and pickling conditions. Note that, in Table 7, t₁ (s) is the time from the end of rough rolling to the start of finish rolling, T₁ (° C.) is the average temperature of the rough bar from the end of rough rolling to the start of finish rolling, and S₁ is the value found by (T₁+273)×(log t₁+20). However, in the formula of S₁, the unit of t₁ is (hr). The finish rolling end temperature was made 930° C. The steel sheet was cooled by 20° C./s up to coiling and was coiled at 550° C. After that, it was cold rolled by a cold rolling machine to obtain a thickness 1.4 mm cold rolled steel sheet. The cold rolled steel sheet was hot dip Al coated to obtain an Al-based coated steel sheet.

The obtained steel sheet was analyzed by GDS (glow discharge optical emission spectrometry) by the following method to evaluate the surface concentration of Cu. The results of evaluation are shown in Table 7.

Degree of Surface Concentration of Cu

The degree of surface concentration of Cu was measured by the following procedure. GDS (glow discharge optical emission spectrometry) was performed in the thickness direction from the surface of the Al-based coated steel sheet to detect the content of Cu. At this time, the value of the maximum value of the content of Cu within a depth of 30 μm from the surface of the steel sheet divided by the content of Cu at a depth of 200 μm from the surface of the steel sheet was calculated to find the degree of surface concentration of Cu. Note that the measurement by GDS was performed at five random points at a position of ¼ of the sheet width (short side) from an end of the Al-based coated steel sheet in the width direction. The average was made the degree of surface concentration of Cu. Note that, regarding the “surface of the steel sheet” referred to here, GDS was performed from the surface of the Al-based coated steel sheet and the depth where Fe became 90% was deemed the surface of the steel sheet.

Invention Examples C1 to C29 satisfying the scope of the present invention turned out to exhibit a good degree of Cu surface concentration and average crystal grain size, but Comparative Examples c1 to c20 not satisfying the scope of the present invention turned out to not satisfy at least one of the degree of Cu surface concentration and average crystal grain size.

TABLE 9 Table 7 Steel sheet Hot rolling Pickling Degree of Cu Average crystal t1 T1 Conc. Temp. Time surface grain size Symbol Steel no. (s) (° C.) S1 Acid (%) (° C.) (s) concentration (μm) Inv. ex. C1 A1 12 1020 22657 Hydrochloric 12 90 30 1.3 25 C2 A2 12 1020 22657 Hydrochloric 12 90 30 1.5 27 C3 A3 12 1020 22657 Hydrochloric 12 90 30 1.3 24 C4 A4 12 1020 22657 Hydrochloric 12 90 30 1.5 22 C5 A5 12 1020 22657 Hydrochloric 12 90 30 1.3 23 C6 A6 12 1020 22657 Hydrochloric 12 90 30 1.5 28 C7 A7 12 1020 22657 Hydrochloric 12 90 30 1.3 24 C8 A8 12 1020 22657 Hydrochloric 12 90 30 1.4 22 C9 A9 12 1020 22657 Hydrochloric 12 90 30 1.3 21 C10 A10 12 1020 22657 Hydrochloric 12 90 30 1.4 28 C11 A11 12 1020 22657 Hydrochloric 12 90 30 1.5 20 C12 A12 12 1020 22657 Hydrochloric 12 90 30 1.3 27 C13 A13 12 1020 22657 Hydrochloric 12 90 30 1.4 23 C14 A14 12 1020 22657 Hydrochloric 12 90 30 1.2 25 C15 A15 12 1020 22657 Hydrochloric 12 90 30 2.0 24 C16 A16 12 1020 22657 Hydrochloric 12 90 30 1.4 27 C17 A17 12 1020 22657 Hydrochloric 12 90 30 1.6 28 C18 A18 12 1020 22657 Hydrochloric 12 90 30 1.4 24 C19 A19 12 1020 22657 Hydrochloric 12 90 30 1.5 23 C20 A20 12 1020 22657 Hydrochloric 12 90 30 1.3 22 C21 A21 12 1020 22657 Hydrochloric 12 90 30 1.4 23 C22 A22 12 1020 22657 Hydrochloric 12 90 30 1.3 25 C23 A23 12 1020 22657 Hydrochloric 12 90 30 1.4 21 C24 A24 12 1020 22657 Hydrochloric 12 90 30 1.4 24 C25 A25 12 1020 22657 Hydrochloric 12 90 30 1.5 23 C26 A26 12 1020 22657 Hydrochloric 12 90 30 1.4 23 C27 A27 12 1020 22657 Hydrochloric 12 90 30 1.6 21 C28 A28 12 1020 22657 Hydrochloric 12 90 30 1.3 25 C29 A29 12 1020 22657 Hydrochloric 12 90 30 1.4 23 Comp. ex. c1 a1 12 1020 22657 Hydrochloric 12 90 30 0.7 25 c2 a2 12 1020 22657 Hydrochloric 12 90 30 0.8 26 c3 a3 12 1020 22657 Hydrochloric 12 90 30 0.7 28 c4 a4 12 1020 22657 Hydrochloric 12 90 30 0.8 24 c5 a5 12 1020 22657 Hydrochloric 12 90 30 0.7 28 c6 a6 12 1020 22657 Hydrochloric 12 90 30 1.0 25 c7 a7 12 1020 22657 Hydrochloric 12 90 30 0.9 28 c8 a8 12 1020 22657 Hydrochloric 12 90 30 0.9 30 c9 a9 12 1020 22657 Hydrochloric 12 90 30 0.7 28 c10 a10 12 1020 22657 Hydrochloric 12 90 30 0.8 67 c11 a11 12 1020 22657 Hydrochloric 12 90 30 0.7 25 c12 a12 12 1020 22657 Hydrochloric 12 90 30 0.8 65 c13 a13 12 1020 22657 Hydrochloric 12 90 30 0.9 27 c14 A30 12 1020 22657 Hydrochloric 12 90 30 0.3 26 c15 A31 12 1020 22657 Hydrochloric 12 90 30 0.8 25 c16 a15 12 1020 22657 Hydrochloric 12 90 30 1.0 28 c17 a16 12 1020 22657 Hydrochloric 12 90 30 0.8 26 c18 a17 12 1020 22657 Hydrochloric 12 90 30 0.8 25 c19 a18 12 1020 22657 Hydrochloric 12 90 30 0.8 24 c20 a19 12 1020 22657 Hydrochloric 12 90 30 0.9 26

Example 3

Each slab of the above Table 1 and Table 2 was hot rolled to obtain a thickness 3.0 mm hot rolled steel sheet. In the hot rolling process, the slab heating temperature was made 1250° C. and the slab was hot rolled and pickled to obtain hot rolled steel sheet. Table 7 shows the hot rolling and pickling conditions. Note that, in Table 7, t₁ (s) is the time from the end of rough rolling to the start of rolling, T₁ (° C.) is the average temperature of the rough bar from the end of rough rolling, and S₁ is the value found by (T₁+273)×(log t₁+20). However, in the formula of S₁, the unit of t₁ is (hr). The end temperature of finish rolling was made 930° C., the steel sheet was cooled at 20° C./s up to coiling, and the steel sheet was coiled at 550° C.

After that, the steel sheet was cold rolled by a cold rolling machine to obtain thickness 1.4 mm cold rolled steel sheet. The cold rolled steel sheet was hot dip Al coated to obtain an Al-based coated steel sheet. Further, among the types of steel shown in Table 1 and Table 2, some were processed by the above processes to obtain cold rolled steel sheet and the cold rolled steel sheet was electroplated including corrosion resistance elements, then was hot dip Al coated to obtain Al-based coated steel sheet having an intermediate layer containing corrosion resistance elements in a total of 30% or more on the surface of the cold rolled steel sheet. The hot rolling, pickling, and coating conditions are shown in Table 8 and Table 9 while the concentration of elements of the intermediate layers are shown in Tables 10-1 to 11-2. Note that, A, B, and C in the columns “hot dip Al coating” of Table 8 and Table 9 respectively mean the following coatings:

A: hot dip Al coating by a usual coating bath (not including corrosion resistance elements)

B: hot dip Al coating by a coating bath with a total content of corrosion resistance elements of more than 0% and less than 1.0%

C: hot dip Al coating by a coating bath with a total content of corrosion resistance elements of 1.0% or more

Invention Examples D1 to D45 satisfying the scope of the present invention turned out to exhibit good total content of corrosion resistance elements at the intermediate layer or good total content of corrosion resistance elements at the Al-based coating, but Comparative Examples d1 to d20 not satisfying the scope of the present invention turned out to not satisfy at least one of the total content of corrosion resistance elements at the intermediate layer and total content of corrosion resistance elements at the Al-based coating.

TABLE 10 Table 8 Electroplating including Hot rolling Pickling corrosion Hot dip t1 T1 Conc. Temp. Time resistance Al Symbol Steel no. (s) (° C.) S1 Acid (%) (° C.) (s) elements coating Inv. ex. D1 A1 12 1020 22657 Hydrochloric 12 90 30 Yes A D2 A2 12 1020 22657 Hydrochloric 12 90 30 Yes A D3 A3 12 1020 22657 Hydrochloric 12 90 30 Yes A D4 A4 12 1020 22657 Hydrochloric 12 90 30 Yes A D5 A5 12 1020 22657 Hydrochloric 12 90 30 Yes A D6 A6 12 1020 22657 Hydrochloric 12 90 30 Yes A D7 A7 12 1020 22657 Hydrochloric 12 90 30 Yes A D8 A8 12 1020 22657 Hydrochloric 12 90 30 Yes A D9 A9 12 1020 22657 Hydrochloric 12 90 30 Yes A D10 A10 12 1020 22657 Hydrochloric 12 90 30 Yes A D11 A11 12 1020 22657 Hydrochloric 12 90 30 Yes A D12 A12 12 1020 22657 Hydrochloric 12 90 30 Yes A D13 A13 12 1020 22657 Hydrochloric 12 90 30 Yes A D14 A14 12 1020 22657 Hydrochloric 12 90 30 Yes A D15 A15 12 1020 22657 Hydrochloric 12 90 30 — C D16 A16 12 1020 22657 Hydrochloric 12 90 30 — C D17 A17 12 1020 22657 Hydrochloric 12 90 30 — C D18 A18 12 1020 22657 Hydrochloric 12 90 30 — C D19 A19 12 1020 22657 Hydrochloric 12 90 30 — C D20 A20 12 1020 22657 Hydrochloric 12 90 30 — C D21 A21 12 1020 22657 Hydrochloric 12 90 30 — C D22 A22 12 1020 22657 Hydrochloric 12 90 30 — C D23 A23 12 1020 22657 Hydrochloric 12 90 30 — C D24 A24 12 1020 22657 Hydrochloric 12 90 30 — C D25 A25 12 1020 22657 Hydrochloric 12 90 30 — C D26 A26 12 1020 22657 Hydrochloric 12 90 30 — C D27 A27 12 1020 22657 Hydrochloric 12 90 30 — C D28 A28 12 1020 22657 Hydrochloric 12 90 30 Yes C D29 A29 12 1020 22657 Hydrochloric 12 90 30 Yes C D30 A30 12 1020 22657 Hydrochloric 12 90 30 Yes C D31 A30 12 1020 22657 Hydrochloric 12 90 30 Yes B D32 A30 12 1020 22657 Hydrochloric 12 90 30 Yes C D33 A30 12 1020 22657 Hydrochloric 12 90 30 Yes C D34 A31 12 1020 22657 Hydrochloric 12 90 30 Yes C D35 A31 12 1020 22657 Hydrochloric 12 90 30 Yes B D36 A31 12 1020 22657 Hydrochloric 12 90 30 Yes C D37 A31 12 1020 22657 Hydrochloric 12 90 30 Yes C D38 a4 12 1020 22657 Hydrochloric 12 90 30 Yes B D39 a9 12 1020 22657 Hydrochloric 12 90 30 Yes B D40 a10 12 1020 22657 Hydrochloric 12 90 30 Yes B D41 a15 12 1020 22657 Hydrochloric 12 90 30 Yes C D42 a16 12 1020 22657 Hydrochloric 12 90 30 Yes C D43 a17 12 1020 22657 Hydrochloric 12 90 30 Yes C D44 a18 12 1020 22657 Hydrochloric 12 90 30 Yes C D45 a19 12 1020 22657 Hydrochloric 12 90 30 Yes C

TABLE 11 Table 9 Electroplating including Hot rolling Pickling corrosion Hot dip t1 T1 Conc. Temp. Time resistance Al Symbol Steel no. (s) (° C.) S1 Acid (%) (° C.) (s) elements coating Comp. ex. d1 a1 12 1020 22657 Hydrochloric 12 90 30 — A d2 a2 12 1020 22657 Hydrochloric 12 90 30 — A d3 a3 12 1020 22657 Hydrochloric 12 90 30 — A d4 a4 12 1020 22657 Hydrochloric 12 90 30 — A d5 a5 12 1020 22657 Hydrochloric 12 90 30 — A d6 a6 12 1020 22657 Hydrochloric 12 90 30 — A d7 a7 12 1020 22657 Hydrochloric 12 90 30 — A d8 a8 12 1020 22657 Hydrochloric 12 90 30 Yes A d9 a9 12 1020 22657 Hydrochloric 12 90 30 Yes A d10 a10 12 1020 22657 Hydrochloric 12 90 30 Yes A d11 a11 12 1020 22657 Hydrochloric 12 90 30 Yes A d12 a12 12 1020 22657 Hydrochloric 12 90 30 Yes A d13 a13 12 1020 22657 Hydrochloric 12 90 30 Yes A d14 a14 12 1020 22657 Hydrochloric 12 90 30 Yes A d16 a15 12 1020 22657 Hydrochloric 12 90 30 — B d17 a16 12 1020 22657 Hydrochloric 12 90 30 — B d18 a17 12 1020 22657 Hydrochloric 12 90 30 — B d19 a18 12 1020 22657 Hydrochloric 12 90 30 — B d20 a19 12 1020 22657 Hydrochloric 12 90 30 — B

TABLE 12 Table 10-1 Coated steel sheet Total content of corrosion Cu content Mo content Ni content Mn content Cr content resistance Si content in in in in in elements in in Intermediate intermediate intermediate intermediate intermediate intermediate intermediate intermediate layer layer layer layer layer layer layer layer thickness Symbol (mass %) (mass %) (mass %) (mass %) (mass %) (mass %) (mass %) (μm) Inv. ex. D1 21 4 2 2 3 32 0 20 D2 23 2 3 2 3 33 0 20 D3 22 3 2 5 2 34 0 20 D4 21 3 3 3 5 35 0 20 D5 20 5 1 5 1 32 0 20 D6 25 2 6 2 4 39 0 20 D7 19 5 1 3 5 33 15 20 D8 22 3 5 5 3 38 15 30 D9 23 8 2 1 3 37 15 30 D10 20 4 9 3 3 39 15 30 D11 22 1 2 8 1 34 15 30 D12 21 1 2 2 9 35 15 30 D13 24 6 0 8 0 38 15 30 D14 21 5 1 5 0 32 15 30 D15 — — — — — — — — D16 — — — — — — — — D17 — — — — — — — — D18 — — — — — — — — D19 — — — — — — — — D20 — — — — — — — — D21 — — — — — — — — D22 — — — — — — — — D23 — — — — — — — — D24 — — — — — — — — D25 — — — — — — — — D26 — — — — — — — — D27 — — — — — — — — D28 22 3 4 2 3 34 0 15 D29 23 5 7 0 0 35 0 15 D30 31 0 0 15 2 48 0 15 D31 30 16 0 3 0 49 0 15 D32 1 0 1 0 0 2 0 15 D33 2 10 5 10 5 32 0 15 D34 30 0 2 16 0 48 0 25 D35 31 17 1 0 1 50 0 25 D36 2 0 1 0 0 3 0 25 D37 2 8 7 7 10 34 0 25 D38 28 10 2 3 2 45 12 35 D39 29 2 11 3 2 47 12 35 D40 30 2 2 12 3 49 12 35 D41 1 0 0 0 1 2 12 20 D42 2 2 0 0 0 4 12 20 D43 2 0 1 0 0 3 12 20 D44 2 0 0 3 0 5 12 20 D45 1 0 0 0 2 3 12 20

TABLE 13 Table 10-2 Coated steel sheet Total content of corrosion Cu content Mo content Ni content Mn content Cr content resistance Si content Al-based in Al-based in Al-based in Al-based in Al-based in Al-based elements in Al- in Al-based coating coating coating coating coating coating based coating coating thickness Symbol (mass %) (mass %) (mass %) (mass %) (mass %) (mass %) (mass %) (μm) Inv. ex. D1 — — — — — — — 20 D2 — — — — — — — 20 D3 — — — — — — — 20 D4 — — — — — — — 20 D5 — — — — — — — 20 D6 — — — — — — — 20 D7 — — — — — — — 20 D8 — — — — — — — 20 D9 — — — — — — — 20 D10 — — — — — — — 20 D11 — — — — — — — 20 D12 — — — — — — — 20 D13 — — — — — — — 20 D14 — — — — — — — 20 D15 4.0 2.0 0.5 0.4 0.1 7.0 10 30 D16 3.0 0.1 1.6 0.1 0.2 5.0 10 30 D17 5.0 0.5 0.1 2.2 0.2 8.0 10 30 D18 4.0 0.1 0.1 0.2 1.6 6.0 10 30 D19 3.0 0.8 0.8 0.2 0.2 5.0 10 30 D20 5.0 0.2 1.3 1.2 0.3 8.0 10 30 D21 5.0 0.2 0.3 1.5 2.0 9.0 10 30 D22 4.0 0.8 0.2 0.9 0.1 6.0 10 60 D23 5.0 2.5 0.1 0.1 2.3 10.0 0 60 D24 2.0 0.4 0.2 0.3 0.1 3.0 0 60 D25 4.0 0.5 0.6 0.4 0.5 6.0 0 60 D26 2.0 0.4 0.3 0.6 0.7 4.0 0 60 D27 2.0 0.2 0.3 0.3 0.2 3.0 0 60 D28 3.0 0.3 0.2 0.3 0.2 4.0 0 20 D29 4.0 0.4 0.1 0.4 0.1 5.0 0 20 D30 3.0 0.3 0.3 1.9 0.5 6.0 8 20 D31 0.2 0.1 0.1 0.0 0.0 0.4 8 20 D32 3.0 0.0 2.5 0.2 2.3 8.0 8 20 D33 0.6 0.4 0.6 0.8 0.6 3.0 8 20 D34 2.0 0.0 0.1 4.8 0.1 7.0 8 10 D35 0.2 0.3 0.0 0.0 0.0 0.5 8 10 D36 4.0 0.0 3.0 0.2 2.8 10.0 8 10 D37 0.8 0.5 0.4 0.5 0.8 3.0 8 10 D38 0.1 0.1 0.0 0.0 0.0 0.2 10 15 D39 0.2 0.0 0.2 0.0 0.0 0.4 10 15 D40 0.1 0.0 0.0 0.2 0.0 0.3 10 15 D41 8.0 0.3 0.3 0.2 3.2 12.0 10 30 D42 8.0 2.5 0.2 0.2 0.1 11.0 10 30 D43 10.0 0.2 3.5 0.2 0.1 14.0 10 30 D44 5.0 0.5 0.3 3.6 0.6 10.0 10 30 D45 6.0 0.8 0.2 0.8 3.2 11.0 10 30

TABLE 11-1 Coated steel sheet Total content of Cu content Mo content Ni content Mn content Cr content corrosion Si content in in in in in resistance in Intermediate intermediate intermediate intermediate intermediate intermediate elements in intermediate layer layer layer layer layer layer intermediate layer layer thickness Symbol (mass %) (mass %) (mass %) (mass %) (mass %) (mass %) (mass %) (μm) Comp. d1 — — — — — — — — ex. d2 — — — — — — — — d3 — — — — — — — — d4 — — — — — — — — d5 — — — — — — — — d6 — — — — — — — — d7 — — — — — — — — d8 1 1 1 0 0 3 0 10 d9 1 0 1 1 1 4 0 10 d10 2 0 1 1 1 5 0 10 d11 2 1 2 1 1 7 0 10 d12 2 1 2 2 1 8 15 40 d13 2 1 0 2 0 5 15 40 d14 2 1 0 0 1 4 15 40 d16 — — — — — — — — d17 — — — — — — — — d18 — — — — — — — — d19 — — — — — — — — d20 — — — — — — — —

TABLE 11-2 Coated steel sheet Total content of corrosion resistance Cu content Mo content Ni content Mn content Cr content elements in Si content Al-based in Al-based in Al-based in Al-based in Al-based in Al-based Al-based in Al-based coating coating coating coating coating coating coating coating thickness Symbol (mass %) (mass %) (mass %) (mass %) (mass %) (mass %) (mass %) (μm) Comp. d1 — — — — — — — 40 ex. d2 — — — — — — — 40 d3 — — — — — — — 40 d4 — — — — — — — 80 d5 — — — — — — — 80 d6 — — — — — — — 80 d7 — — — — — — — 80 d8 — — — — — — — 40 d9 — — — — — — — 40 d10 — — — — — — — 40 d11 — — — — — — — 40 d12 — — — — — — — 20 d13 — — — — — — — 20 d14 — — — — — — — 20 d16 0.2 0.0 0.1 0.0 0.0 0.3 0 30 d17 0.2 0.1 0.0 0.1 0.0 0.4 0 30 d18 0.1 0.0 0.0 0.1 0.1 0.3 0 30 d19 0.1 0.1 0.0 0.0 0.0 0.2 10 30 d20 0.1 0.0 0.0 0.0 0.0 0.1 10 30

Example 4

Slabs having the steel constituents of Steel Nos. A28 and A29 in the types of steel shown in Table 1 and Table 2 were hot rolled (some heated using bar heater), pickled (hydrochloric acid or sulfuric acid), and hot dip Al coated as shown in Table 8 to manufacture Al-based coated steel sheets (thickness 2.8 mm)

The results of evaluation of the structures of the obtained steel sheets are shown in Table 12.

Invention Examples El to E22 satisfying the scope of the present invention turned out to exhibit good degree of Cu surface concentration and average crystal grain size, but Comparative Examples e1 to e18 not satisfying the scope of the present invention turned out to not satisfy at least one of the degree of Cu surface concentration and average crystal grain size.

TABLE 12 Hot rolling Steel sheet Finish Degree Average Slab rolling of Cu crystal heating end Cooling Coiling Pickling surface grain Steel temp t₁ T₁ Bar temp. rate temp. Conc. Temp. Time concen- size Symbol no. (° C.) (s) (° C.) S₁ heater (° C.) (° C./s) (° C.) Acid (%) (° C.) (s) tration (μm) Inv. E1 A28 1130 10 1050 23078 Yes 960 22 570 Hydrochloric 12 90 30 1.3 21 ex. E2 A28 1320 13 1040 23053 No 920 17 540 Hydrochloric 12 90 30 1.3 28 E3 A28 1270 8 950 21215 No 940 18 560 Hydrochloric 12 90 30 1.2 22 E4 A28 1280 10 1020 22555 No 850 17 590 Hydrochloric 12 90 30 1.3 28 E5 A28 1250 10 1040 22904 Yes 980 19 580 Hydrochloric 12 90 30 1.3 27 E6 A28 1280 12 1040 23008 No 910 12 620 Hydrochloric 12 90 30 1.3 27 E7 A28 1290 19 1020 22915 No 920 23 690 Hydrochloric 12 90 30 1.2 28 E8 A28 1250 12 1020 22657 No 930 20 550 Hydrochloric 12 90 30 1.3 25 E9 A28 1250 12 1020 22657 No 930 20 550 Sulfuric 10 80 60 1.3 25 E10 A28 1250 12 1020 22657 No 930 20 550 Hydrochloric 8 90 30 1.5 25 E11 A28 1250 12 1020 22657 No 930 20 550 Hydrochloric 7 80 150 1.3 25 E12 A29 1130 10 1050 23078 Yes 960 22 570 Hydrochloric 12 90 30 1.4 22 E13 A29 1320 13 1040 23053 No 920 17 540 Hydrochloric 12 90 30 1.4 27 E14 A29 1270 8 950 21215 No 940 18 560 Hydrochloric 12 90 30 1.3 21 E15 A29 1280 10 1020 22555 No 850 17 590 Hydrochloric 12 90 30 1.4 28 E16 A29 1250 10 1040 22904 Yes 980 19 580 Hydrochloric 12 90 30 1.4 27 E17 A29 1280 12 1040 23008 No 910 12 620 Hydrochloric 12 90 30 1.4 27 E18 A29 1290 19 1020 22915 No 920 23 690 Hydrochloric 12 90 30 1.3 28 E19 A29 1250 12 1020 22657 No 930 20 550 Hydrochloric 12 90 30 1.4 23 E20 A29 1250 12 1020 22657 No 930 20 550 Sulfuric 10 80 60 1.4 23 E21 A29 1250 12 1020 22657 No 930 20 550 Hydrochloric 8 90 30 1.6 23 E22 A29 1250 12 1020 22657 No 930 20 550 Hydrochloric 7 80 150 1.4 23 Comp. e1 A28 1380 14 1030 22920 No 930 18 590 Hydrochloric 12 90 30 1.3 92 ex. e2 A28 1260 5 880 19765 Yes 940 16 600 Hydrochloric 12 90 30 1.0 24 e3 A28 1260 5 800 18394 Yes 940 16 600 Hydrochloric 12 90 30 0.7 23 e4 A28 1270 10 980 21857 No 750 17 610 Hydrochloric 12 90 30 1.2 82 e5 A28 1250 12 960 21606 Yes 1100 15 590 Hydrochloric 12 90 30 1.2 80 e6 A28 1260 14 960 21688 No 950 3 580 Hydrochloric 12 90 30 1.2 74 e7 A28 1270 10 960 21508 No 940 19 850 Hydrochloric 12 90 30 1.2 75 e8 A28 1270 10 960 21508 No 940 19 600 Sulfuric 15 80 180 0.9 24 e9 A28 1270 10 960 21508 No 940 19 600 Hydrochloric 10 90 180 1.0 24 e10 A29 1380 14 1030 22920 No 930 18 590 Hydrochloric 12 90 30 1.3 78 e11 A29 1260 5 880 19765 Yes 940 16 600 Hydrochloric 12 90 30 1.0 22 e12 A29 1260 5 800 18394 Yes 940 16 600 Hydrochloric 12 90 30 0.8 21 e13 A29 1270 5 980 21480 No 750 17 610 Hydrochloric 12 90 30 1.2 74 e14 A29 1250 6 980 21579 Yes 1100 15 590 Hydrochloric 12 90 30 1.2 76 e15 A29 1260 8 980 21736 No 950 3 580 Hydrochloric 12 90 30 1.2 74 e16 A29 1270 8 980 21736 No 940 19 850 Hydrochloric 12 90 30 1.2 75 e17 A29 1270 8 980 21736 No 940 19 600 Hydrochloric 12 90 90 1.0 22 e18 A29 1270 8 980 21736 No 940 19 600 Hydrochloric 10 90 180 1.1 22

Example 5

The types of steel shown in Table 1 and Table 2 were used to manufacture coated steel sheets (thickness 1.8 mm) under the hot rolling, pickling, and plating conditions shown in Table 13 and Table 14. The intermediate layers of the coated steel sheets and the contents of the corrosion resistance elements in the Al-based coating are shown in Tables 15-1 to 16-2. Note that, A, B, and C in the columns “hot dip Al coating” of Table 13 and Table 14 respectively mean the following coating:

A: hot dip Al coating by a usual coating bath (not including corrosion resistance elements)

B: hot dip Al coating by a coating bath with a total content of corrosion resistance elements of more than 0% and less than 1.0%

C: hot dip Al coating by a coating bath with a total content of corrosion resistance elements of 1.0% or more

Next, these coated steel sheets were heat treated under the conditions of Table 17 and Table 18 to manufacture coated steel members. The results of evaluation of the structures and properties of the obtained coated steel members are shown in Tables 19-1 to 20-2.

Invention Examples F1 to F38 satisfying the scope of the present invention turned out to be good in both the concentration of corrosion resistance elements in the Al—Fe-based coatings and the properties, but Comparative Examples f1 to f24 not satisfying the scope of the present invention turned out to not satisfy the concentration of corrosion resistance elements in the Al—Fe-based coatings.

TABLE 13 Al electroplating including Hot rolling Picking corrosion Hot dip Steel t₁ T₁ Conc. Temp. Time resistance Al Symbol no. (s) (° C.) S₁ Acid (%) (° C.) (s) elements coating F1 A28 12 1020 22657 Hydrochloric 12 90 30 — A F2 A28 12 1020 22657 Hydrochloric 12 90 30 — A F3 A28 12 1020 22657 Hydrochloric 12 90 30 — A F4 A28 12 1020 22657 Hydrochloric 12 90 30 — A F5 A28 12 1020 22657 Hydrochloric 12 90 30 — A F6 A28 12 1020 22657 Hydrochloric 12 90 30 — A F7 A28 12 1020 22657 Hydrochloric 12 90 30 — A F8 A28 12 1020 22657 Hydrochloric 12 90 30 — A F9 A28 12 1020 22657 Hydrochloric 12 90 30 — A F10 A29 12 1020 22657 Hydrochloric 12 90 30 — A F11 A29 12 1020 22657 Hydrochloric 12 90 30 — A F12 A29 12 1020 22657 Hydrochloric 12 90 30 — A F13 A29 12 1020 22657 Hydrochloric 12 90 30 — A F14 A29 12 1020 22657 Hydrochloric 12 90 30 — A F15 A29 12 1020 22657 Hydrochloric 12 90 30 — A F16 A29 12 1020 22657 Hydrochloric 12 90 30 — A F17 A29 12 1020 22657 Hydrochloric 12 90 30 — A F18 A29 12 1020 22657 Hydrochloric 12 90 30 — A F19 A30 12 1020 22657 Hydrochloric 12 90 30 Yes C F20 A30 12 1020 22657 Hydrochloric 12 90 30 Yes B F21 A30 12 1020 22657 Hydrochloric 12 90 30 Yes C F22 A30 12 1020 22657 Hydrochloric 12 90 30 Yes C F23 A31 12 1020 22657 Hydrochloric 12 90 30 Yes C F24 A31 12 1020 22657 Hydrochloric 12 90 30 Yes B F25 A31 12 1020 22657 Hydrochloric 12 90 30 Yes C F26 A31 12 1020 22657 Hydrochloric 12 90 30 Yes C F27 a4 12 1020 22657 Hydrochloric 12 90 30 Yes B F28 a9 12 1020 22657 Hydrochloric 12 90 30 Yes B F29 a10 12 1020 22657 Hydrochloric 12 90 30 Yes B F30 a15 12 1020 22657 Hydrochloric 12 90 30 Yes C F31 a16 12 1020 22657 Hydrochloric 12 90 30 Yes C F32 a17 12 1020 22657 Hydrochloric 12 90 30 Yes C F33 a18 12 1020 22657 Hydrochloric 12 90 30 Yes C F34 a19 12 1020 22657 Hydrochloric 12 90 30 Yes C F35 A28 12 1020 22657 Hydrochloric 12 90 30 Yes C F36 A29 12 1020 22657 Hydrochloric 12 90 30 Yes C F37 A28 5 880 19765 Sulfuric 15 80 180 Yes A F38 A29 5 880 19765 Hydrochloric 12 90 90 Yes A

TABLE 14 Al electroplating including Hot rolling Picking corrosion Hot Steel t₁ T₁ Conc. Temp. Time resistance dip Al Symbol no. (s) (° C.) S₁ Acid (%) (° C.) (s) elements coating f1 A28 12 1020 22657 Hydrochloric 12 90 30 — A f2 A28 12 1020 22657 Hydrochloric 12 90 30 — A f3 A28 12 1020 22657 Hydrochloric 12 90 30 — A f4 A28 12 1020 22657 Hydrochloric 12 90 30 — A f5 A28 12 1020 22657 Hydrochloric 12 90 30 — A f6 A28 12 1020 22657 Hydrochloric 12 90 30 — A f7 A28 12 1020 22657 Hydrochloric 12 90 30 — A f8 A29 12 1020 22657 Hydrochloric 12 90 30 — A f9 A29 12 1020 22657 Hydrochloric 12 90 30 — A f10 A29 12 1020 22657 Hydrochloric 12 90 30 — A f11 A29 12 1020 22657 Hydrochloric 12 90 30 — A f12 A29 12 1020 22657 Hydrochloric 12 90 30 — A f13 A28 12 1020 22657 Hydrochloric 12 90 30 Yes C f14 A28 12 1020 22657 Hydrochloric 12 90 30 Yes C f15 A28 12 1020 22657 Hydrochloric 12 90 30 Yes C f16 A28 12 1020 22657 Hydrochloric 12 90 30 Yes C f17 A28 12 1020 22657 Hydrochloric 12 90 30 Yes C f18 A28 12 1020 22657 Hydrochloric 12 90 30 Yes C f19 A28 12 1020 22657 Hydrochloric 12 90 30 Yes C f20 A29 12 1020 22657 Hydrochloric 12 90 30 Yes C f21 A29 12 1020 22657 Hydrochloric 12 90 30 Yes C f22 A29 12 1020 22657 Hydrochloric 12 90 30 Yes C f23 A29 12 1020 22657 Hydrochloric 12 90 30 Yes C f24 A29 12 1020 22657 Hydrochloric 12 90 30 Yes C

TABLE 15-1 Coated steel sheet Total content of corrosion resistance Cu content in Mo content in Ni content in Mn content in Cr content in elements in Degree of Cu Grain intermediate intermediate intermediate intermediate intermediate intermediate surface size layer layer layer layer layer layer Symbol concentration (μm) (mass %) (mass %) (mass %) (mass %) (mass %) (mass %) F1 1.3 25 — — — — F2 1.3 25 — — — — — — F3 1.3 25 — — — — — — F4 1.3 25 — — — — — — F5 1.3 25 — — — — — — F6 1.3 25 — — — — — — F7 1.3 25 — — — — — — F8 1.3 25 — — — — — — F9 1.3 25 — — — — — — F10 1.3 23 — — — — — — F11 1.3 23 — — — — — — F12 1.3 23 — — — — — — F13 1.4 23 — — — — — — F14 1.4 23 — — — — — — F15 1.4 23 — — — — — — F16 1.4 23 — — — — — — F17 1.4 23 — — — — — — F18 1.4 23 — — — — — — F19 0.3 26 31 0 0 15 2 48 F20 0.3 26 30 16 0 3 0 49 F21 0.3 26 1 0 1 0 0 2 F22 0.3 26 2 10 5 10 5 32 F23 0.8 25 30 0 2 16 0 48 F24 0.8 25 31 17 1 0 1 50 F25 0.8 25 2 0 1 0 0 3 F26 0.8 25 2 8 7 7 10 34 F27 0.8 24 28 10 2 3 2 45 F28 0.7 28 29 2 11 3 2 47 F29 0.8 67 30 2 2 12 3 49 F30 0.8 26 1 0 0 0 1 2 F31 0.8 25 2 2 0 0 0 4 F32 0.8 24 2 0 1 0 0 3 F33 0.8 24 2 0 0 3 0 5 F34 0.9 26 1 0 0 0 2 3 F35 1.3 25 22 3 4 2 3 34 F36 1.4 23 23 5 7 0 0 35 F37 0.9 24 21 4 2 2 3 32 F38 1.0 22 23 2 3 2 3 33

TABLE 15-2 Coated steel sheet Total content of Cu content Mo content Ni content Mn content Cr content corrosion resistance in Al-based in Al-based in Al-based in Al-based in Al-based elements in coating coating coating coating coating Al-based coating Symbol (mass %) (mass %) (mass %) (mass %) (mass %) (mass %) F1 — — — — — — F2 — — — — — — F3 — — — — — — F4 — — — — — — F5 — — — — — — F6 — — — — — — F7 — — — — — — F8 — — — — — — F9 — — — — — — F10 — — — — — — F11 — — — — — — F12 — — — — — — F13 — — — — — — F14 — — — — — — F15 — — — — — — F16 — — — — — — F17 — — — — — — F18 — — — — — — F19 3.0 0.3 0.3 1.9 0.5 6.0 F20 0.2 0.1 0.1 0.0 0.0 0.4 F21 3.0 0.0 2.5 0.2 2.3 8.0 F22 0.6 0.4 0.6 0.8 0.6 3.0 F23 2.0 0.0 0.1 4.8 0.1 7.0 F24 0.2 0.3 0.0 0.0 0.0 0.5 F25 4.0 0.0 3.0 0.2 2.8 10.0 F26 0.8 0.5 0.4 0.5 0.8 3.0 F27 0.1 0.1 0.0 0.0 0.0 0.2 F28 0.2 0.0 0.2 0.0 0.0 0.4 F29 0.1 0.0 0.0 0.2 0.0 0.3 F30 8.0 0.3 0.3 0.2 3.2 12.0 F31 8.0 2.5 0.2 0.2 0.1 11.0 F32 10.0 0.2 3.5 0.2 0.1 14.0 F33 5.0 0.5 0.3 3.6 0.6 10.0 F34 6.0 0.8 0.2 0.8 3.2 11.0 F35 3.0 0.3 0.2 0.3 0.2 4.0 F36 4.0 0.4 0.1 0.4 0.1 5.0 F37 — — — — — — F38 — — — — — —

TABLE 16-1 Coated steel sheet Total content of corrosion Cu content in Mo content in Ni content in Mn content in Cr content in resistance Degree of Cu Grain intermediate intermediate intermediate intermediate intermediate elements in surface size layer layer layer layer layer intermediate layer Symbol concentration (μm) (mass %) (mass %) (mass %) (mass %) (mass %) (mass %) f1 1.3 25 — — — — f2 1.3 25 — — — — — — f3 1.3 25 — — — — — — f4 1.3 25 — — — — — — f5 1.3 25 — — — — — — f6 1.3 25 — — — — — — f7 1.3 25 — — — — — — f8 1.4 23 — — — — — — f9 1.4 23 — — — — — — f10 1.4 23 — — — — — — f11 1.4 23 — — — — — — f12 1.4 23 — — — — — — f13 1.3 25 22 3 4 2 3 34 f14 1.3 25 22 3 4 2 3 34 f15 1.3 25 22 3 4 2 3 34 f16 1.3 25 22 3 4 2 3 34 f17 1.3 25 22 3 4 2 3 34 f18 1.3 25 22 3 4 2 3 34 f19 1.3 25 22 3 4 2 3 34 f20 1.4 23 23 5 7 0 0 35 f21 1.4 23 23 5 7 0 0 35 f22 1.4 23 23 5 7 0 0 35 f23 1.4 23 23 5 7 0 0 35 f24 1.4 23 23 5 7 0 0 35

TABLE 16-2 Coated steel sheet Total content of corrosion resistance Cu content Mo content N content Mn content Cr content elements in in Al-based in Al-based in Al-based in Al-based in Al-based Al-based coating coating coating coating coating coating Symbol (mass %) (mass %) (mass %) (mass %) (mass %) (mass %) f1 — — — — — — f2 — — — — — — f3 — — — — — — f4 — — — — — — f5 — — — — — — f6 — — — — — — f7 — — — — — — f8 — — — — — — f9 — — — — — — f10 — — — — — — f11 — — — — — — f12 — — — — — — f13 3.0 0.3 0.2 0.3 0.2 4.0 f14 3.0 0.3 0.2 0.3 0.2 4.0 f15 3.0 0.3 0.2 0.3 0.2 4.0 f16 3.0 0.3 0.2 0.3 0.2 4.0 f17 3.0 0.3 0.2 0.3 0.2 4.0 f18 3.0 0.3 0.2 0.3 0.2 4.0 f19 3.0 0.3 0.2 0.3 0.2 4.0 f20 4.0 0.4 0.1 0.4 0.1 5.0 f21 4.0 0.4 0.1 0.4 0.1 5.0 f22 4.0 0.4 0.1 0.4 0.1 5.0 f23 4.0 0.4 0.1 0.4 0.1 5.0 f24 4.0 0.4 0.1 0.4 0.1 5.0

TABLE 17 Heat treatment Heating Rate of Ms to temp. temperature Cooling rate 100° C. T₂ rise t₂ down to Ms cooling rate Symbol (° C.) (° C./s) (s) S₂ (° C./s) (° C./s) F1 850 10 30 19946 95 50 F2 1080 12 20 23831 90 55 F3 990 7 30 22455 100 40 F4 870 500 40 20446 90 45 F5 900 8 3 19679 90 55 F6 920 10 30 21200 35 50 F7 910 9 40 21168 50 8 F8 920 10 100 21819 100 50 F9 920 10 90 21765 100 30 F10 850 10 50 20193 95 50 F11 1050 12 20 23299 90 55 F12 990 7 30 22455 100 40 F13 870 500 40 20446 90 45 F14 900 8 4 19824 90 55 F15 920 10 30 21200 35 50 F16 910 9 40 21168 50 8 F17 920 10 80 21704 100 50 F18 920 10 90 21765 100 25 F19 920 10 90 21765 100 25 F20 920 10 90 21765 100 25 F21 920 10 90 21765 100 25 F22 920 10 90 21765 100 25 F23 920 10 90 21765 100 25 F24 920 10 90 21765 100 25 F25 920 10 90 21765 100 25 F26 920 10 90 21765 100 25 F27 920 10 90 21765 100 25 F28 920 10 90 21765 100 25 F29 920 10 90 21765 100 25 F30 920 10 90 21765 100 25 F31 920 10 90 21765 100 25 F32 920 10 90 21765 100 25 F33 920 10 90 21765 100 25 F34 920 10 90 21765 100 25 F35 920 10 90 21765 100 25 F36 920 10 90 21765 100 25 F37 920 10 90 21765 100 25 F38 920 10 90 21765 100 25

TABLE 18 Heat treatment Heating Rate of Cooling Ms to temp. temperature rate down 100° C. T₂ rise t₂ to Ms cooling rate Symbol (° C.) (° C./s) (s) S₂ (° C./s) (° C./s) f1 810 10 10 18717 120 60 f2 970 2 0.05 18671 100 45 f3 870 1500 1 18631 110 55 f4 870 9 1 18631 105 40 f5 870 9 0.1 17498 105 40 f6 910 10 0.5 18935 5 50 f7 960 8 0.1 18888 60 1 f8 800 10 5 18223 120 60 f9 980 2 0.01 17954 100 45 f10 870 1500 0.2 17839 110 55 f11 920 10 0.3 18834 5 50 f12 980 8 0.05 18822 60 1 f13 810 10 4 18290 120 60 f14 940 2 0.05 18217 100 45 f15 850 1500 1 18302 110 55 f16 850 9 1 18302 105 40 f17 850 9 0.1 17189 105 40 f18 890 10 0.5 18612 5 50 f19 940 8 0.1 18579 60 1 f20 800 10 2 17800 120 60 f21 960 2 0.01 17665 100 45 f22 850 1500 0.2 17524 110 55 f23 900 10 0.3 18516 5 50 f24 960 8 0.05 18519 60 1

TABLE 19-1 Coated steel member Maximum Maximum Maximum Maximum Maximum Concentration Maximum Al—Fe- Cu content Mo content Ni content Mn content Cr content of resistance Si content corrosion in Al—Fe- in Al—Fe- in Al—Fe- in Al—Fe- in Al—Fe- elements in in Al—Fe- based based based based based based Al—Fe-based based coating coating coating coating coating coating coating coating thickness Symbol (mass %) (mass %) (mass %) (mass %) (mass %) (mass %) (mass %) (μm) Inv. F1 0.16 0.15 0.00 0.62 0.00 0.17 11 30 ex. F2 0.18 0.20 0.00 0.83 0.00 0.19 12 30 F3 0.17 0.20 0.00 0.91 0.00 0.18 12 30 F4 0.16 0.16 0.00 0.71 0.00 0.17 11 30 F5 0.13 0.10 0.00 0.52 0.00 0.14 11 30 F6 0.16 0.19 0.00 0.80 0.00 0.17 12 30 F7 0.16 0.18 0.00 0.79 0.00 0.17 12 30 F8 0.16 0.18 0.00 0.78 0.00 0.17 12 30 F9 0.16 0.19 0.00 0.81 0.00 0.17 12 30 F10 0.20 0.13 0.16 0.60 0.14 0.21 9 30 F11 0.21 0.10 0.20 0.74 0.23 0.22 10 30 F12 0.22 0.14 0.18 0.70 0.18 0.23 10 30 F13 0.19 0.13 0.15 0.66 0.15 0.20 10 30 F14 0.14 0.10 0.12 0.49 0.12 0.15 9 30 F15 0.20 0.15 0.17 0.65 0.15 0.21 9 30 F16 0.19 0.14 0.16 0.62 0.15 0.20 10 30 F17 0.20 0.14 0.17 0.66 0.14 0.21 10 30 F18 0.21 0.14 0.17 0.67 0.16 0.22 10 30 F19 0.31 0.15 0.21 3.00 0.00 0.35 0 35 F20 0.21 2.50 0.21 0.36 0.00 0.23 0 35 F21 0.20 0.15 1.00 0.36 1.60 0.24 0 35 F22 0.10 1.20 0.80 1.50 1.20 0.15 0 35 F23 0.30 0.10 0.00 5.00 0.12 0.36 0 35 F24 0.23 2.00 0.00 0.39 0.12 0.25 0 35 F25 0.21 0.10 1.00 0.39 2.00 0.25 0 35 F26 0.11 1.50 1.20 2.00 0.80 0.17 0 35 F27 0.24 0.55 0.29 1.36 0.40 0.27 0 50 F28 0.22 0.19 1.05 0.77 0.00 0.24 0 50 F29 0.24 0.14 0.00 1.89 0.20 0.27 0 50 F30 0.24 0.03 0.00 0.72 0.00 0.25 8 50 F31 0.25 2.68 0.27 0.89 1.06 0.29 10 50 F32 0.24 0.72 0.00 0.67 1.96 0.28 8 50 F33 0.23 0.21 0.68 0.59 0.30 0.25 15 50 F34 0.25 0.19 0.22 1.32 0.34 0.27 11 50 F35 0.27 0.35 0.18 0.95 0.12 0.29 0 35 F36 0.34 0.50 0.41 1.20 0.45 0.37 0 35 F37 0.17 0.17 0.06 0.57 0.03 0.18 0 20 F38 0.22 0.21 0.20 0.59 0.17 0.23 0 20

TABLE 19-2 Coated steel member Average Al Average Fe Minimum Cu content in content in content in Max/min Al—Fe-based Al—Fe-based Al—Fe-based Cu in Tensile CCT coating coating coating Al—Fe-based strength No. of Symbol (mass %) (mass %) (mass %) coating (MPa) cycles Inv. F1 33 59 0.09 1.8 1945 276 ex. F2 33 58 0.09 2.0 1903 360 F3 32 59 0.09 1.9 1902 360 F4 33 59 0.07 2.3 1949 264 F5 33 59 0.06 2.2 1941 204 F6 32 59 0.08 2.0 1947 360 F7 32 59 0.08 2.0 1789 360 F8 32 59 0.08 2.0 1936 360 F9 32 59 0.08 2.0 1937 360 F10 35 58 0.11 1.8 2145 252 F11 35 58 0.11 1.9 2103 360 F12 34 59 0.11 2.0 2102 360 F13 35 58 0.09 2.1 2149 258 F14 35 58 0.06 2.3 2141 204 F15 35 58 0.11 1.8 2147 360 F16 35 58 0.10 1.9 1920 360 F17 35 58 0.11 1.8 2135 360 F18 35 58 0.12 1.8 2136 360 F19 40 59 0.17 1.8 2102 270 F20 41 58 0.09 2.3 2102 171 F21 40 59 0.14 1.4 2100 172 F22 41 58 0.06 1.7 2104 162 F23 40 59 0.17 1.8 2195 240 F24 41 58 0.10 2.3 2192 165 F25 41 58 0.14 1.5 2194 165 F26 41 58 0.07 1.6 2190 162 F27 40 59 0.11 2.2 2700 165 F28 40 59 0.10 2.2 2230 222 F29 40 59 0.12 2.0 2523 192 F30 35 59 0.16 1.5 2310 183 F31 35 58 0.17 1.5 2335 234 F32 36 58 0.16 1.5 2436 219 F33 32 58 0.15 1.5 2345 227 F34 33 59 0.17 1.5 2513 213 F35 40 59 0.14 1.9 1937 360 F36 40 59 0.18 1.9 2136 360 F37 40 59 0.06 2.8 1937 360 F38 40 59 0.09 2.4 2136 360

TABLE 20-1 Coated steel member Concentration Maximum Maximum Maximum Maximum Maximum of corrosion Maximum Cu content Mo content Ni content Mn content Cr content resistance Si content Al—Fe- in Al—Fe- in Al—Fe- in Al—Fe- in Al—Fe- in Al—Fe- elements in in Al—Fe- based based based based based based Al—Fe-based based coating coating coating coating coating coating coating coating thickness Symbol (mass %) (mass %) (mass %) (mass %) (mass %) (mass %) (mass %) (μm) Comp. f1 0.09 0.14 0.00 0.55 0.00 0.10 10 30 ex. f2 0.09 0.16 0.00 0.65 0.00 0.10 10 30 f3 0.08 0.15 0.00 0.58 0.00 0.09 10 30 f4 0.09 0.15 0.00 0.60 0.00 0.10 10 30 f5 0.08 0.08 0.00 0.33 0.00 0.08 10 30 f6 0.08 0.16 0.00 0.61 0.00 0.09 10 30 f7 0.09 0.16 0.00 0.63 0.00 0.10 10 30 f8 0.09 0.09 0.13 0.49 0.10 0.10 9 30 f9 0.09 0.12 0.15 0.56 0.11 0.10 9 30 f10 0.09 0.10 0.13 0.50 0.11 0.10 9 30 f11 0.09 0.12 0.14 0.58 0.12 0.10 9 30 f12 0.10 0.11 0.15 0.57 0.13 0.11 9 30 f13 0.09 0.12 0.05 0.32 0.03 0.10 0 35 f14 0.09 0.11 0.05 0.32 0.03 0.10 0 35 f15 0.09 0.12 0.05 0.32 0.03 0.10 0 35 f16 0.09 0.12 0.06 0.32 0.03 0.10 0 35 f17 0.08 0.13 0.06 0.31 0.04 0.09 0 35 f18 0.10 0.11 0.06 0.31 0.04 0.11 0 35 f19 0.09 0.12 0.05 0.31 0.04 0.10 0 35 f20 0.09 0.17 0.13 0.39 0.15 0.10 0 35 f21 0.09 0.16 0.13 0.39 0.14 0.10 0 35 f22 0.08 0.16 0.14 0.40 0.14 0.09 0 35 f23 0.10 0.16 0.14 0.40 0.14 0.11 0 35 f24 0.10 0.17 0.13 0.40 0.14 0.11 0 35

TABLE 20-2 Coated steel member Average Al Average Fe Minimum Cu content in content in content in Max/min Al—Fe-based Al—Fe-based Al—Fe-based Cu in Tensile CCT coating coating coating Al—Fe-based strength No. of Symbol (mass %) (mass %) (mass %) coating (MPa) cycles Comp. f1 34 59 0.04 2.3 1646 117 ex. f2 34 59 0.05 1.8 1901 108 f3 34 59 0.03 2.7 1953 105 f4 34 59 0.05 1.8 1945 99 f5 34 59 0.04 2.0 1940 97 f6 34 59 0.04 2.0 824 360 f7 34 59 0.04 2.3 1445 183 f8 35 58 0.04 2.3 1826 93 f9 35 58 0.05 1.8 2081 87 f10 35 58 0.05 1.8 2133 81 f11 35 58 0.05 1.8 1004 348 f12 35 58 0.05 2.0 1480 165 f13 40 59 0.05 1.8 1657 126 f14 40 59 0.05 1.8 1907 114 f15 40 59 0.04 2.3 1942 105 f16 40 59 0.04 2.3 1936 105 f17 40 59 0.03 2.7 1927 97 f18 40 59 0.04 2.5 834 360 f19 40 59 0.04 2.3 1450 186 f20 41 58 0.05 1.8 1838 93 f21 41 58 0.05 1.8 2089 87 f22 41 58 0.03 2.7 2124 81 f23 41 58 0.04 2.5 994 360 f24 41 58 0.04 2.5 1485 168

INDUSTRIAL APPLICABILITY

According to the present invention, it becomes possible to obtain a coated steel member and steel sheet excellent in hydrogen embrittlement resistance in a corrosive environment. The coated steel member according to the present invention is particularly suitable for a frame part of an automobile. 

1. A coated steel sheet for hot stamping having a layer where Cu is concentrated at a surface of a steel sheet, having a degree of Cu surface concentration at the layer where Cu is concentrated of 1.2 or more, further having an Al-based coating on the layer where Cu is concentrated, and having an average crystal grain size of the steel sheet of 30 μm or less; here, the “degree of Cu surface concentration” shows the ratio of (maximum content of Cu in range from surface of steel sheet to depth of 0 to 30 μm)/(average content of Cu from surface of steel sheet to depth of 200 μm), while the “surface of steel sheet” means the position of a depth where the Fe content becomes 90% when performing GDS from the surface of the coated steel sheet in the thickness direction.
 2. A coated steel sheet for hot stamping comprised of a steel sheet, an intermediate layer positioned on a surface of the steel sheet, and an Al-based coating positioned on a surface of the intermediate layer, the intermediate layer containing Cu, the intermediate layer containing Cu and one or more of Mo, Ni, Mn, and Cr in a total by mass % of 30% or more.
 3. The coated steel sheet for hot stamping according to claim 1 wherein a chemical composition of the steel sheet comprises, by mass %, C: 0.25 to 0.60%, Si: 0.25 to 2.00%, Mn: 0.30 to 3.00%, P: 0.050% or less, S: 0.0100% or less, N: 0.010% or less, Ti: 0.010 to 0.100%, B: 0.0005 to 0.0100%, Mo: 0.10 to 1.00%, Cu: 0.01 to 1.00%, Cr: 0 to 1.00%, Ni: 0 to 1.00%, V: 0 to 1.00%, Ca: 0 to 0.010%, Al: 0 to 1.00%, Nb: 0 to 0.10%, Sn: 0 to 1.00%, W: 0 to 1.00%, Sb: 0 to 1.00%, REMs: 0 to 0.30%, and balance: Fe and impurities.
 4. The coated steel sheet for hot stamping according to claim 2 wherein a chemical composition of the steel sheet comprises, by mass %, C: 0.25 to 0.60%, Si: 0.25 to 2.00%, Mn: 0.30 to 3.00%, P: 0.050% or less, S: 0.0100% or less, N: 0.010% or less, Ti: 0.010 to 0.100%, B: 0.0005 to 0.0100%, Mo: 0.10 to 1.00%, Cu: 0.01 to 1.00%, Cr: 0 to 1.00%, Ni: 0 to 1.00%, V: 0 to 1.00%, Ca: 0 to 0.010%, Al: 0 to 1.00%, Nb: 0 to 0.10%, Sn: 0 to 1.00%, W: 0 to 1.00%, Sb: 0 to 1.00%, REMs: 0 to 0.30%, and balance: Fe and impurities.
 5. A method for manufacturing the coated steel sheet for hot stamping according to claim 1, the method comprising the steps of: heating a slab at 1100 to 1350° C., hot rolling the heated slab to obtain hot rolled steel sheet under conditions where, when defining a time t₁(hr) from an end of rough rolling to a start of finish rolling and an average temperature T₁(° C.) of a rough bar from the end of rough rolling to the start of finish rolling, (T₁+273)×(log t₁+20)≥20000 and a finish rolling end temperature becomes an Ar₃ point to 1000° C., cooling the above hot rolled steel sheet by an average cooling rate of 10° C./s, coiling the steel sheet after cooling at 700° C. or less, and pickling the steel sheet after coiling, wherein in the step of pickling, hydrochloric acid or sulfuric acid is used, a pickling temperature is 80 to 90° C., and an acid concentration α (%) and pickling time “t” (s) satisfy 6≤α<14, 0<t≤420−30×α. 